Stress corrosion cracking in single crystals of Ag-Au alloy

被引：10

作者：

Alvarez, MG ^{[1
]}

Fernández, SA ^{[1
]}

Galvele, JR ^{[1
]}

机构：

[1] Comis Nacl Energia Atom, Dept Mat, RA-1429 Buenos Aires, DF, Argentina

来源：

CORROSION SCIENCE | 2000年 / 42卷 / 04期

关键词：

alloy; silver; stress corrosion;

D O I：

10.1016/S0010-938X(99)00107-9

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Single crystals of Ag-10Au (at%) were found to be susceptible to transgranular stress corrosion cracking (TGSCC) in 1 M HClO4 and 1 M KCl solutions. The effect of the potential and the strain rate on the stress corrosion crack propagation rare was studied. Results were compared with those obtained for the intergranular stress corrosion cracking (IGSCC) observed in polycrystalline silver-gold alloys under the same experimental conditions, The TGSCC velocity was found to change with the potential in the same way as the IGSCC velocity. Also the increase in the strain rate value led to an increase in the crack propagation rate values. For both TGSCC and IGSCC, a linear relationship between the logarithm of the crack propagation rate and the logarithm of the strain rate was found. The slope of this relationship was always higher for IGSCC than for TGSCC. (C) 2000 Elsevier Science Ltd. All rights reserved.

引用

页码：739 / 752

页数：14

共 12 条

[1] STRESS-CORROSION CRACKING IN SINGLE-CRYSTALS OF FE-25CR-20NI [J].

AHLERS, M ;

RIECKE, E .

CORROSION SCIENCE, 1978, 18 (01) :21-&

[2] SURFACE MOBILITY MECHANISM OF STRESS-CORROSION CRACKING [J].

GALVELE, JR .

CORROSION SCIENCE, 1993, 35 (1-4) :419-434

[3] Stress corrosion cracking of silver-gold alloys in 1 M potassium chloride, potassium bromide, and potassium iodide solutions [J].

Galvele, JR ;

Maier, IA ;

Fernandez, SA .

CORROSION, 1996, 52 (05) :326-330

[4] ENHANCED SURFACE MOBILITY AS THE CAUSE OF STRESS-CORROSION CRACKING [J].

GALVELE, JR .

JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1986, 133 (05) :953-954

[5] NOTES ON THE SURFACE MOBILITY MECHANISM OF STRESS-CORROSION CRACKING - COMMENT [J].

GALVELE, JR .

CORROSION SCIENCE, 1994, 36 (05) :901-910

[6] A STRESS-CORROSION CRACKING MECHANISM BASED ON SURFACE MOBILITY [J].

GALVELE, JR .

CORROSION SCIENCE, 1987, 27 (01) :1-33

[7]

GALVELE JR, 1993, METALL T A, V24, P425

[8]

GALVELE JR, 1995, MOD ASPECT ELECTROC, V27, P233

[9] The effect of Cu2+ concentration on the stress corrosion cracking susceptibility of α-brass in cupric nitrate solutions [J].

Giordano, CM ;

Duffo, GS ;

Galvele, JR .

CORROSION SCIENCE, 1997, 39 (10-11) :1915-1923

[10] Mechanistic studies of stress corrosion cracking: Application of the corrosion-assisted cleavage model to results using oriented single crystals [J].

Lichter, BD ;

Flanagan, WF ;

Kim, JS ;

Elkenbracht, C ;

vanHunen, M .

CORROSION, 1996, 52 (06) :453-463

← 1 2 →