Modeling of degradation effects considering side reactions for a pouch type Li-ion polymer battery with carbon anode

被引:95
作者
Fu, Rujian [1 ]
Choe, Song-Yul [1 ]
Agubra, Victor [2 ]
Fergus, Jeffrey [2 ]
机构
[1] Auburn Univ, Auburn, AL 36849 USA
[2] Auburn Univ, Mat Res & Educ Ctr, Wilmore Labs 273, Auburn, AL 36849 USA
关键词
Li ion polymer battery; Degradation model; Side reactions; SEI; Deposits; Capacity fade; CAPACITY FADE; CYCLE-LIFE; MECHANISMS; LICOO2; PERFORMANCE; GROWTH;
D O I
10.1016/j.jpowsour.2014.03.045
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
When a lithium ion polymer battery (LiPB) is being cycled, one major cause for degradations is the irreversible side reactions between ions and solvent of electrolyte taking place at the surface of anode particles. SEM analysis of cycled battery cells has revealed that the deposits from the side reactions are dispersed not only on particles, but also between the composite anode and the separator. Thus, the solid electrolyte interface (SEI) becomes thicker and extra deposit layers are formed between composite anode and separator. Also, XPS analysis showed that the deposits are composed of Li2CO3, which is ionic conductive and electronic nonconductive. Based on the mechanisms and findings, we identified four degradation parameters, including volume fraction of accessible active anode, SEI resistance, resistance of deposit layer and diffusion coefficient of electrolyte, to describe capacity and power fade caused by the side reactions. These degradation parameters have been incorporated into an electrochemical thermal model that has been previously developed. The terminal voltage and capacity of the integrated model are compared with experimental data obtained for up to 300 cycles. Finally, the resistance of the deposit layer calculated by the model is validated against the thickness of the deposit layer measured by SEM. (C) 2014 Elsevier B.V. All rights reserved.
引用
收藏
页码:120 / 135
页数:16
相关论文
共 36 条
[1]   Surface changes on LiNi0.8Co0.2O2 particles during testing of high-power lithium-ion cells [J].
Abraham, DP ;
Twesten, RD ;
Balasubramanian, M ;
Petrov, I ;
McBreen, J ;
Amine, K .
ELECTROCHEMISTRY COMMUNICATIONS, 2002, 4 (08) :620-625
[2]   Design criteria for nanostructured Li-ion batteries [J].
Aifantis, K. E. ;
Hackney, S. A. ;
Dempsey, J. P. .
JOURNAL OF POWER SOURCES, 2007, 165 (02) :874-879
[3]   Stable crack growth in nanostructured Li-batteries [J].
Aifantis, KE ;
Dempsey, JP .
JOURNAL OF POWER SOURCES, 2005, 143 (1-2) :203-211
[4]   Capacity fade mechanisms and side reactions in lithium-ion batteries [J].
Arora, P ;
White, RE ;
Doyle, M .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1998, 145 (10) :3647-3667
[5]   Failure and stabilization mechanisms of graphite electrodes [J].
Aurbach, D ;
Levi, MD ;
Levi, E ;
Schechter, A .
JOURNAL OF PHYSICAL CHEMISTRY B, 1997, 101 (12) :2195-2206
[6]   An EIS study of the anode Li/PEO-LiTFSI of a Li polymer battery [J].
Bouchet, R ;
Lascaud, S ;
Rosso, M .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 2003, 150 (10) :A1385-A1389
[7]   Factors that affect cycle-life and possible degradation mechanisms of a Li-ion cell based on LiCoO2 [J].
Choi, SS ;
Lim, HS .
JOURNAL OF POWER SOURCES, 2002, 111 (01) :130-136
[8]   ION BOMBARDMENT-INDUCED DECOMPOSITION OF LI AND BA SULFATES AND CARBONATES STUDIED BY X-RAY PHOTOELECTRON-SPECTROSCOPY [J].
CONTARINI, S ;
RABALAIS, JW .
JOURNAL OF ELECTRON SPECTROSCOPY AND RELATED PHENOMENA, 1985, 35 (3-4) :191-201
[9]  
CONTOUR JP, 1979, J MICROSC SPECT ELEC, V4, P483
[10]   Modeling, validation and analysis of mechanical stress generation and dimension changes of a pouch type high power Li-ion battery [J].
Fu, Rujian ;
Xiao, Meng ;
Choe, Song-Yul .
JOURNAL OF POWER SOURCES, 2013, 224 :211-224