Breakdown of dynamic scaling in thin film binary liquids undergoing phase separation

The kinetics of phase separation in thin polymer blend films displaying discrete and bicontinuous domain morphologies are examined. For discrete domains, the correlation length xi grows as t(1/3), in agreement with a coalescence model. By plotting xi/d vs t/t(i) (initiation time), universal growth behavior is obtained for thickness values (d) from 1000 to 190 nm. In contrast, bicontinuous domains grow with a decreasing exponent, 0.62 to 0.28, as d decreases from 900 to 90 nm (i.e., no universal growth). This slowing down with reduced dimensionality suggests suppression of lateral hydrodynamic pumping.