The influence of the phosphorus content on the bioactivity of sol-gel glass ceramics

被引：107

作者：

Padilla, S ^{[1
]}

Román, J ^{[1
]}

Carenas, A ^{[1
]}

Vallet-Regí, M ^{[1
]}

机构：

[1] Univ Complutense Madrid, Fac Farm, Dept Quim Inorgan & Bioinorgan, E-28040 Madrid, Spain

来源：

BIOMATERIALS | 2005年 / 26卷 / 05期

关键词：

glass-ceramics; sol-gel glasses; bioactivity; in vitro test; calcium silicate;

D O I：

10.1016/j.biomaterials.2004.02.054

中图分类号：

R318 [生物医学工程];

学科分类号：

0831 ;

摘要：

The aim of this work was to study the influence of the phosphorus oil the crystallization and bioactivity of glass-ceramics obtained from sol-gel glasses. For this purpose two sol-gel glasses with a similar composition but one of them containing P2O5 (70% SiO2; 30% CaO and 70% SiO2; 26% CaO; 4% P2O5, mol%) were prepared. Pieces of these glasses were treated at temperatures ranging between 700degreesC and 1400degreesC for 3 h. The obtained materials were characterized by XRD, FTIR, SEM-EDS and the biaxial flexural strength was determined in samples heated at 1100degreesC. In addition, an in vitro bioactivity study in simulated body fluid (SBF) was carried out. The results showed that phosphorus plays an important role in the crystallization of the glasses: it induced the crystallization of calcium phosphate phases, the stabilization of the wollastonite phase at high temperature as well as the crystallization of SiO2 phases at low ternperatures. Moreover, the presence of phosphorus produced a heterogeneous distribution of defects in the pieces and, therefore, the flexural strength of samples containing this element decreased. Finally, glass-ceramics obtained from glasses containing phosphorus showed the fastest formation rate of the apatite layer when soaked in SBF. (C) 2004 Elsevier Ltd. All rights reserved.

引用

页码：475 / 483

页数：9