Rapid synthesis of dense Ti3SiC2 by spark plasma sintering

被引：140

作者：

Gao, NF

Li, JT

Zhang, D

Miyamoto, Y ^{[1
]}

机构：

[1] Osaka Univ, Joining & Welding Res Inst, Ibaraki, Osaka 5670047, Japan

[2] Univ Sci & Technol Beijing, Lab Special Cerma & PM, Beijing 100083, Peoples R China

[3] Shanghai Jiao Tong Univ, State Key Lab Met Matrix Composites, Shanghai 200030, Peoples R China

来源：

JOURNAL OF THE EUROPEAN CERAMIC SOCIETY | 2002年 / 22卷 / 13期

关键词：

mechanical properties; microstructure-final; reactive synthesis; Ti3SiC2; X-ray diffraction; SPS;

D O I：

10.1016/S0955-2219(02)00021-3

中图分类号：

TQ174 [陶瓷工业]; TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

Ti3SiC2 was rapidly synthesized and simultaneously consolidated from the starting mixture of Ti/Si/2TiC by spark plasma sintering (SPS). An intensive reaction leading to the formation of Ti3SiC2 occurred at the measured temperature of around 1200 degreesC, which is several hundreds degrees lower than that of conventional reactive hot pressing. The phase composition of the product could be tailored by adjusting the process parameters. An axisymmetric preferred orientation of the Ti3SiC2 grains with well-developed (008) planes was formed, resulting in an anisotropic hardness in respect to the textured product. (C) 2002 Elsevier Science Ltd. All rights reserved.