Cleaved end-face quality of microstructured polymer optical fibres

The cutting of a microstructured polymer optical fibre to form an optical end-face is studied. The effect of the temperature and speed of the cutting blade on the end-face is qualitatively assessed and it is found that for fibres at temperatures in the range 70-90 degrees C, a blade at a similar temperature moving at a speed of less than 0.5 mm/s produces a good quality end-face. The nature of the damage caused by the cutting process was examined and found to vary with fibre temperature, blade quality and cut depth. Thermo-mechanical analysis showed that the drawn material was significantly more visco-elastic than the annealed raw material in the 70-90 degrees C temperature range. The behaviour of the surface damage with cut depth was found to be consistent with the behaviour of a visco-elastic material. (c) 2006 Elsevier B.V. All rights reserved.