Surface activation of wood for graft polymerisation

被引：31

作者：

Hill, CAS ^{[1
]}

Cetin, NS ^{[1
]}

机构：

[1] Univ Wales, Sch Agr & Forest Sci, Bangor LL57 2UW, Gwynedd, Wales

来源：

INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES | 2000年 / 20卷 / 01期

关键词：

adhesives for wood; wood; adhesion by chemical bonding; anhydride modification;

D O I：

10.1016/S0143-7496(99)00017-2

中图分类号：

TQ [化学工业];

学科分类号：

0817 ;

摘要：

An investigation of graft polymerisation of wood surfaces chemically modified with propionic, crotonic, or methacrylic anhydride has been undertaken. All samples exhibited weight gains when reacted with styrene in the presence of a free-radical initiator. However, solid-state NMR and FTIR evidence showed that there was only grafting of monomer in the case of methacrylic anhydride modified wood. With the other two modifications, it is clear that the styrene is in intimate contact with the wood, but that there is no chemical bond. Wood flour modified with crotonic anhydride followed by styrene grafting was heated with aqueous NaOH. Following such treatment, it was observed that the ester bond was readily hydrolysed. However, with methacrylic modified and styrene grafted samples, the ester bond was resistant to hydrolysis. Lap joints were formed by hot pressing veneers of modified wood with monomer (styrene or methyl methacrylate) plus initiator at the interface. Extremely strong bonds were found in the case of methacrylic anhydride modified samples. (C) 2000 Elsevier Science Ltd. All rights reserved.

引用

页码：71 / 76

页数：6

共 11 条

[1]

Banks W.B., 1994, CELLULOSIC POLYM BLE, P131

[2] FIBER ACTIVATION AND SUBSEQUENT CO-POLYMERIZATION [J].

BANKS, WB ;

DIN, RH ;

OWEN, NL .

HOLZFORSCHUNG, 1995, 49 (02) :104-108

[3]

HON DNS, 1996, CHEM MODIFICATION LI

[4]

MATSUDA H, 1987, WOOD SCI TECHNOL, V21, P75

[5] PREPARATION AND CROSSLINKING OF OLIGOESTERIFIED WOODS BASED ON PHTHALIC-ANHYDRIDE AND GLYCIDYL METHACRYLATE [J].

MATSUDA, H ;

UEDA, M ;

MORI, H .

WOOD SCIENCE AND TECHNOLOGY, 1988, 22 (04) :335-344

[6] PREPARATION AND CROSSLINKING OF OLIGOESTERIFIED WOODS BASED ON MALEIC-ANHYDRIDE AND ALLYL GLYCIDYL ETHER [J].

MATSUDA, H ;

UEDA, M ;

MORI, H .

WOOD SCIENCE AND TECHNOLOGY, 1988, 22 (01) :21-32

[7] THE ACTIVATION OF WOOD FIBER FOR THERMOPLASTIC COUPLING, THE REACTION OF WOOD WITH A POTENTIAL COUPLING AGENT [J].

QUINNEY, RF ;

BANKS, WB ;

LAWTHER, JM .

JOURNAL OF WOOD CHEMISTRY AND TECHNOLOGY, 1995, 15 (04) :529-544

[8]

Rowell R. M., 1983, Forest Products Abstracts, V6, P363

[9] FTIR CHARACTERIZATION OF CHEMICALLY-MODIFIED FIBERBOARD [J].

ROZMAN, HD ;

BANKS, WB ;

LAWTHER, MI .

INTERNATIONAL JOURNAL OF POLYMERIC MATERIALS, 1994, 26 (1-2) :19-24

[10] Chemical modification of wood with maleic anhydride and subsequent copolymerization with diallyl phthalate [J].

Rozman, HD ;

Kumar, RN ;

Khalil, HPSA ;

Abusamah, A ;

Abu, R .

JOURNAL OF WOOD CHEMISTRY AND TECHNOLOGY, 1997, 17 (04) :419-433

← 1 2 →