Effects of chromium on the glass formation and corrosion behavior of bulk glassy Fe-Cr-Mo-C-B alloys

被引：57

作者：

Pang, S ^{[1
]}

Zhang, T ^{[1
]}

Asami, K ^{[1
]}

Inoue, A ^{[1
]}

机构：

[1] Tohoku Univ, Inst Mat Res, Sendai, Miyagi 9808577, Japan

来源：

MATERIALS TRANSACTIONS | 2002年 / 43卷 / 08期

关键词：

bulk glassy alloy; iron -based alloy; chromium; supercooled liquid; corrosion; X-ray photoelectron spectroscopy (XPS); passive film;

D O I：

10.2320/matertrans.43.2137

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Bulk glassy Fe60-xCrxMo15C15B10 (x = 0, 7.5, 15, 22.5 and 30 at%) alloys with high thermal stability were synthesized and the effects of chromium on the glass formation and corrosion behavior were clarified. The maximum diameter for glass formation is 2-2.5 mm for the 7.5 and 15 at%Cr alloys and 1 mm for the other alloys. In the present glassy alloy system, the temperature interval of the supercooled liquid region (DeltaT(x)) changed with chromium and was enlarged from around 70 K at x = 0, 22.5 and 30 at% to over 80 K at x = 7.5 and 15 at%. Both corrosion rate and anodic current density by potentiodynamic polarization in HCl solutions decreased with an increase of chromium content in the alloys. For the Cr-free alloy, molybdenum was significantly concentrated in the surface film after immersion in 1N HCl solution. The bulk glassy alloys containing chromium was immune to corrosion by the formation of protective passive film enriched with chromium during immersion in the solution.

引用

页码：2137 / 2142

页数：6

共 30 条

[11] AL-LA-NI AMORPHOUS-ALLOYS WITH A WIDE SUPERCOOLED LIQUID REGION [J].

INOUE, A ;

ZHANG, T ;

MASUMOTO, T .

MATERIALS TRANSACTIONS JIM, 1989, 30 (12) :965-972

[12] FE-BASED FERROMAGNETIC GLASSY ALLOYS WITH WIDE SUPERCOOLED LIQUID REGION [J].

INOUE, A ;

GOOK, JS .

MATERIALS TRANSACTIONS JIM, 1995, 36 (09) :1180-1183

[13] Thermal and magnetic properties of bulk Fe-based glassy alloys prepared by copper mold casting [J].

Inoue, A ;

Shinohara, Y ;

Gook, JS .

MATERIALS TRANSACTIONS JIM, 1995, 36 (12) :1427-1433

[14] Preparation and thermal stability of bulk amorphous Pd40Cu30Ni10P20 alloy cylinder of 72 mm in diameter [J].

Inoue, A ;

Nishiyama, N ;

Kimura, H .

MATERIALS TRANSACTIONS JIM, 1997, 38 (02) :179-183

[15] Bulk amorphous alloys with high mechanical strength and good soft magnetic properties in Fe-TM-B (TM=IV-VIII group transition metal) system [J].

Inoue, A ;

Zhang, T ;

Takeuchi, A .

APPLIED PHYSICS LETTERS, 1997, 71 (04) :464-466

[16] HIGH-STRENGTH BULK AMORPHOUS-ALLOYS WITH LOW CRITICAL COOLING RATES [J].

INOUE, A .

MATERIALS TRANSACTIONS JIM, 1995, 36 (07) :866-875

[17] ZR-AL-NI AMORPHOUS-ALLOYS WITH HIGH GLASS-TRANSITION TEMPERATURE AND SIGNIFICANT SUPERCOOLED LIQUID REGION [J].

INOUE, A ;

ZHANG, T ;

MASUMOTO, T .

MATERIALS TRANSACTIONS JIM, 1990, 31 (03) :177-183

[18] High-strength Cu-based bulk glassy alloys in Cu-Zr-Ti and Cu-Hf-Ti ternary systems [J].

Inoue, A ;

Zhang, W ;

Zhang, T ;

Kurosaka, K .

ACTA MATERIALIA, 2001, 49 (14) :2645-2652

[19] Thermal stability and soft magnetic properties of Co-Fe-M-B (M=Nb, Zr) amorphous alloys with large supercooled liquid region [J].

Itoi, T ;

Inoue, A .

MATERIALS TRANSACTIONS JIM, 2000, 41 (09) :1256-1262

[20]

*JAP I MET, 1993, MET DAT, P1

← 1 2 3 →