In situ confocal laser scanning microscopy of AA 2024-T3 corrosion metrology -: I.: Localized corrosion of particles

被引:194
作者
Ilevbare, GO [1 ]
Schneider, O [1 ]
Kelly, RG [1 ]
Scully, JR [1 ]
机构
[1] Univ Virginia, Dept Mat Sci & Engn, Ctr Electrochem Sci & Engn, Charlottesville, VA 22904 USA
关键词
D O I
10.1149/1.1764780
中图分类号
O646 [电化学、电解、磁化学];
学科分类号
081704 ;
摘要
The morphology of attack at and around the intermetallic compounds (IMC) present on bare AA 2024-T3 was studied in situ using confocal laser scanning microscopy. Exposures were conducted in 0.1 M Na2SO4 + 0.005 M NaCl at pH 3, 6, and 10 as well as near-neutral 0.5 M NaCl. The types of attack observed could be categorized as matrix and IMC pitting, trenching adjacent to IMC, and matrix etching. The electrochemical behavior of bulk synthesized Al-Cu, Al-Cu-Mg, and Al-Cu-Fe-Mn intermetallic compounds as well as that of AA2024-T3 was used to rationalize the observed attack metrology. The galvanic coupling between the AA2024-T3 matrix and the intermetallic particles controlled the attack rates. In Al-Cu-Mg, the strong polarization to the open-circuit potential of the alloy caused rapid dissolution (ca. 10 mA/cm(2)), whereas for the Al-Cu-Fe-Mn the dissolution rates were on the order of 100 mA/cm(2). The limited dissolution rates of the Al-Cu-Fe-Mn phase were due to the cathodic polarization of these particles by the matrix under open-circuit conditions. Several pits were initiated at large Al-Cu-Mg particles. These pits were stable within the Al-Cu-Mg phase, but could not form stable pits in the alloy matrix during open-circuit corrosion. Calculation of growth rates and pit stability products for the individual IMC emphasized the role of metastable pitting in the observed corrosion metrology, which developed on AA2024-T3 during open-circuit corrosion. (C) 2004 The Electrochemical Society.
引用
收藏
页码:B453 / B464
页数:12
相关论文
共 49 条
[41]   Confocal laser scanning microscopy as a tool for in situ monitoring of corrosion underneath organic coatings [J].
Schneider, O ;
Ilevbare, GO ;
Scully, JR ;
Kelly, RG .
ELECTROCHEMICAL AND SOLID STATE LETTERS, 2001, 4 (12) :B35-B38
[42]  
SCHNEIDER O, UNPUB
[43]   ELECTROCHEMICAL CHARACTERISTICS OF THE AL2CU, AL3TA AND AL3ZR INTERMETALLIC PHASES AND THEIR RELEVANCY TO THE LOCALIZED CORROSION OF AL-ALLOYS [J].
SCULLY, JR ;
KNIGHT, TO ;
BUCHHEIT, RG ;
PEEBLES, DE .
CORROSION SCIENCE, 1993, 35 (1-4) :185-195
[44]  
SCULLY JR, 1992, ELECTROCHEMICAL SOC, V929, P144
[45]   STOCHASTIC THEORY OF PITTING CORROSION [J].
SHIBATA, T ;
TAKEYAMA, T .
CORROSION, 1977, 33 (07) :243-251
[46]  
Suter T, 1999, ELEC SOC S, V98, P118
[47]   Dealloying and corrosion of Al alloy 2024-T3 [J].
Vukmirovic, MB ;
Dimitrov, N ;
Sieradzki, K .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 2002, 149 (09) :B428-B439
[48]   LOCAL CHEMISTRY AND GROWTH OF SINGLE CORROSION PITS IN ALUMINUM [J].
WONG, KP ;
ALKIRE, RC .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1990, 137 (10) :3010-3015
[49]  
ZHANG W, 1998, MURI REPORT, P51