High strength magnesium-based glass matrix composites

被引：12

作者：

Bartusch, B ^{[1
]}

Schurack, F ^{[1
]}

Eckert, J ^{[1
]}

机构：

[1] IFW Dresden, Inst Met Mat, D-01171 Dresden, Germany

来源：

MATERIALS TRANSACTIONS | 2002年 / 43卷 / 08期

关键词：

magnesium alloys; metallic glasses; composites; mechanical alloying; mechanical properties;

D O I：

10.2320/matertrans.43.1979

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Magnesium-based glass matrix composites containing oxide particles were produced by mechanical alloying Of Mg55Cu30Y15 elemental powder mixtures with the addition of MgO, CeO2, Cr2O3 or Y2O3 oxide particles. The formation of the glassy phase was characterized by X-ray-diffraction and transmission electron microscopy methods and was found to proceed almost unaffected by the presence of the oxides. Differential-scanning-calorimetry-analysis revealed, that the amorphous matrix features a wide supercooled liquid region with an extension of about 40-50 K. Differences in the thermal stability of the composites depending on the oxide addition are discussed. Viscosity measurements proved the existence of a characteristic minimum of viscosity in this temperature range which was used to consolidate the powders into bulk samples by uniaxial hot pressing. The deformation behaviour under compression at room temperature as well as at elevated temperature of 423 K yielded excellent properties compared to conventionally produced magnesium-based alloys.

引用

页码：1979 / 1984

页数：6

共 28 条

[21]

MATSUMOTO T, 1975, MATER SCI ENG, V19, P1

[22]

POLMEAR IJ, 1981, LIGHT ALLOYS

[23] Newtonian flow of Zr55Cu30Al10Ni5 bulk metallic glassy alloys [J].

Reger-Leonhard, A ;

Heilmaier, M ;

Eckert, J .

SCRIPTA MATERIALIA, 2000, 43 (05) :459-464

[24] Properties of Mg-Y-Cu glasses with nanocrystalline particles [J].

Schlorke, N ;

Weiss, B ;

Eckert, J ;

Schultz, L .

NANOSTRUCTURED MATERIALS, 1999, 12 (1-4) :127-130

[25]

SCHLORKE N, 1998, P C MAGN ALL THEIR A, P533

[26] MICROSCOPIC MECHANISM FOR STEADY-STATE INHOMOGENEOUS FLOW IN METALLIC GLASSES [J].

SPAEPEN, F .

ACTA METALLURGICA, 1977, 25 (04) :407-415

[27]

SPAEPEN F, 1983, AMORPHOUS METALLIC A, pCH13

[28] Thermal stability and viscosity of Mg-based glasses and composites [J].

Weiss, B ;

Eckert, J .

METASTABLE, MECHANICALLY ALLOYED AND NANOCRYSTALLINE MATERIALS, PTS 1 AND 2, 2000, 343-3 :129-134

← 1 2 3 →