A low-cycle fatigue life prediction model of ultrafine-grained metals

被引：32

作者：

Ding, HZ ^{[1
]}

Mughrabi, H ^{[1
]}

Höppel, HW ^{[1
]}

机构：

[1] Univ Erlangen Nurnberg, Inst Werkstoffwissensch, Lehrstuhl 1, D-91058 Erlangen, Germany

来源：

FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES | 2002年 / 25卷 / 10期

关键词：

crack growth rate; cyclic J integral; fatigue life; low-cycle fatigue; modelling; ultrafine-grained copper;

D O I：

10.1046/j.1460-2695.2002.00564.x

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

A (high strain) low-cycle fatigue (LCF) life prediction model of ultrafine-grained (UFG) metals has been proposed. The microstructure of a UFG metal is treated as a two-phase 'composite' consisting of the 'soft' matrix (all the grain interiors) and the 'hard' reinforcement (all the grain boundaries). The dislocation strengthening of the grain interiors is considered as the major strengthening mechanism in the case of UFG metals. The proposed model is based upon the assumption that there is a fatigue-damaged zone ahead of the crack tip within which the actual degradation of the UFG metal takes place. In high-strain LCF conditions, the fatigue-damaged zone is described as the region in which the local cyclic stress level approaches the ultimate tensile strength of the UFG metal, with the plastic strain localization caused by a dislocation sliding-off process within it. The fatigue crack growth rate is directly correlated to the range of the crack-tip opening displacement. The empirical Coffin-Manson and Basquin relationships are derived theoretically and compared with experimental fatigue data obtained on UFG copper (99.99%) at room temperature under both strain and stress control. Good agreement is found between the model and the experimental data. It is remarkable that, although the model is essentially formulated for high strains (LCF), it is also found to be applicable at low strains in the high-cycle fatigue (HCF) regime.

引用

页码：975 / 984

页数：10

共 29 条

[11]

Heitmann HH., 1985, ADV FRACTURE RES, V5, P3599

[12]

HOEPPEL HW, 2001, MAT WEEK 2000 P

[13] Low cycle fatigue of a copper bicrystal under constant plastic strain control [J].

Hu, YM ;

Wang, ZG .

INTERNATIONAL JOURNAL OF FATIGUE, 1997, 19 (01) :59-65

[14]

LIU HW, 1987, LOW CYCLE FATIGUE EL, P556

[15]

Lowe T., 2000, Investigations and Applications of Severe Plastic Deformation, DOI [10.1007/978-94-011-4062-1_11, DOI 10.1007/978-94-011-4062-1_11]

[16]

MANSON SS, 1170 NACA LEW FLIGHT

[17]

Mughrabi H, 2000, NATO SCI S PRT 3 HI, V80, P241

[18]

Mughrabi H, 2001, MRS P, V634

[19]

POLAK J, 1991, CYCLIC PLASTICITY LO

[20]

Rice J.R., 1967, ASTM SPEC TECH PUBL, V415, P247, DOI 10.1520/STP47234S

← 1 2 3 →