Mode I interlaminar fracture behavior and mechanical properties of CFRPs with nanoclay-filled epoxy matrix

被引:238
作者
Siddiqui, Naveed A.
Woo, Ricky S. C.
Kim, Jang-Kyo
Leung, Christopher C. K.
Munir, Arshad
机构
[1] Hong Kong Univ Sci & Technol, Dept Mech Engn, Kowloon, Hong Kong, Peoples R China
[2] Hong Kong Univ Sci & Technol, Dept Civil Engn, Kowloon, Hong Kong, Peoples R China
[3] Natl Engn & Sci Commiss, Islamabad, Pakistan
关键词
nano-structures; carbon fibre; polymer-matrix composites (PMCs); fracture toughness; delamination;
D O I
10.1016/j.compositesa.2006.03.001
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The mechanical properties and fracture behavior of nanocomposites and carbon fiber composites (CFRPs) containing organoclay in the epoxy matrix have been investigated. Morphological studies using TEM and XRD revealed that the clay particles within the epoxy resin were intercalated or orderly exfoliated. The organoclay brought about a significant improvement in flexural modulus, especially in the first few wt% of loading, and the improvement of flexural modulus was at the expense of a reduction in flexural strength. The quasistatic fracture toughness increased, whereas the impact fracture toughness dropped sharply with increasing the clay content. Flexural properties of CFRPs containing organoclay modified epoxy matrix generally followed the trend similar to the epoxy nanocomposite although the variation was much smaller for the CFRPs. Both the initiation and propagation values of mode I interlaminar fracture toughness of CFRP composites increased with increasing clay concentration. In particular, the propagation fracture toughness almost doubled with 7 wt% clay loading. A strong correlation was established between the fracture toughness of organoclay-modified epoxy matrix and the CFRP composite interlaminar fracture toughness. (c) 2006 Elsevier Ltd. All rights reserved.
引用
收藏
页码:449 / 460
页数:12
相关论文
共 24 条
[1]   Use of layered silicates to supplementarily toughen high performance epoxy-carbon fiber composites [J].
Becker, O ;
Varley, RJ ;
Simon, GP .
JOURNAL OF MATERIALS SCIENCE LETTERS, 2003, 22 (20) :1411-1414
[2]  
Bradley W. L., 1989, Key Engineering Materials, V37, P161
[3]  
Harcup JP, 1999, ANTEC '99: PLASTICS BRIDGING THE MILLENNIA, CONFERENCE PROCEEDINGS, VOLS I-III, P3396
[4]   Epoxy-organoclay nanocomposites: morphology, moisture absorption behavior and thermo-mechanical properties [J].
Hu, CG ;
Kim, JK .
COMPOSITE INTERFACES, 2005, 12 (3-4) :271-289
[5]   Moisture barrier characteristics of organoclay-epoxy nanocomposites [J].
Kim, JK ;
Hu, CG ;
Woo, RSC ;
Sham, ML .
COMPOSITES SCIENCE AND TECHNOLOGY, 2005, 65 (05) :805-813
[6]   HIGH-STRENGTH, HIGH FRACTURE-TOUGHNESS FIBER COMPOSITES WITH INTERFACE CONTROL - A REVIEW [J].
KIM, JK ;
MAI, YW .
COMPOSITES SCIENCE AND TECHNOLOGY, 1991, 41 (04) :333-378
[7]   FRACTURE-TOUGHNESS OF CFRP WITH MODIFIED EPOXY-RESIN MATRICES [J].
KIM, JK ;
BAILLIE, C ;
POH, J ;
MAI, YW .
COMPOSITES SCIENCE AND TECHNOLOGY, 1992, 43 (03) :283-297
[8]  
KIM JK, 1998, ENG INTERFACES FIBER, P330
[9]   FRACTURE-TOUGHNESS AND FAILURE MECHANISMS IN SILICA-FILLED EPOXY-RESIN COMPOSITES - EFFECTS OF TEMPERATURE AND LOADING RATE [J].
KOH, SW ;
KIM, JK ;
MAI, YW .
POLYMER, 1993, 34 (16) :3446-3455
[10]   Synthesis of epoxy-clay nanocomposites: influence of the nature of the clay on structure [J].
Kornmann, X ;
Lindberg, H ;
Berglund, LA .
POLYMER, 2001, 42 (04) :1303-1310