Synthesis, characterization and optical properties of Eu2O3 mesoporous thin films

被引:34
作者
Castro, Yolanda
Julian, Beatriz
Boissiere, Cedric
Viana, Bruno
Amenitsch, Heinz
Grosso, David
Sanchez, Clement
机构
[1] Univ Paris 06, UMR CNRS 7574, Lab Chim Mat Condensee, F-75252 Paris, France
[2] Austrian Acad Sci, Inst Biophys & Xray Struct Res, A-8010 Graz, Austria
关键词
D O I
10.1088/0957-4484/18/5/055705
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
For the first time, nanocrystalline Eu2O3 thin films, exhibiting similar to 50% of porous volume, highly accessible mesoporosity, pore diameter of about 10 nm, and thermal stability up to 830 degrees C, were prepared using the evaporation-induced self-assembly ( EISA) process from europium ( III) chloride and specific polyethylene oxide based copolymer structuring agent. Crystallization of the inorganic network was achieved through a controlled thermal treatment sequence that was followed by in situ time-resolved SAXS/WAXS analysis involving synchrotron radiation. Atomic force microscopy ( AFM) and x-ray diffraction ( XRD) were used to complete the characterization of the crystallization of the film. Porous structures were additionally analysed by transmission electron microscopy ( TEM), and environmental ellipsometry porosimetry ( EEP), while the composition of the films was characterized by Rutherford back-scattering ( RBS). Finally, the luminescence properties of these layers were investigated.
引用
收藏
页数:7
相关论文
共 24 条
[21]  
REISFELD R, 1997, LASERS EXCITED STATE
[22]  
SANCHEZ C, 1990, SPIE P, V1328, P40
[23]  
Shionoya S., 1999, PHOSPHOR HDB
[24]   Synthesis of thermally stable highly ordered nanoporous tin oxide thin films with a 3D face-centered orthorhombic nanostructure [J].
Urade, VN ;
Hillhouse, HW .
JOURNAL OF PHYSICAL CHEMISTRY B, 2005, 109 (21) :10538-10541