Preparation and characterization of zeolite-supported molybdenum and cobalt-molybdenum sulfide catalysts

被引:44
作者
Okamoto, Y [1 ]
机构
[1] Shimane Univ, Dept Mat Sci, Matsue, Shimane 690, Japan
关键词
hydrodesulfurization; Mo sulfide catalysts; Co sulfide catalysts;
D O I
10.1016/S0920-5861(97)00087-4
中图分类号
O69 [应用化学];
学科分类号
081704 ;
摘要
Preparation, characterization and catalysis of zeolite-supported Mo, Co(Ni) and Co(Ni)-Mo sulfide catalysts have been reviewed in the present article. Incomplete sulfidation of Mo oxides and poor dispersion of Mo sulfides were observed for zeolite-supported Mo catalysts prepared by impregnation methods, accompanied by a considerable crystallinity loss at a high calcination temperature. A significant migration of Mo oxide species into zeolite pores was noted during the calcination, producing Mo ore-species in tetrahedral coordinations. Incorporation of Mo into zeolite using ion-exchange techniques and solid-solid reactions is briefly described. Metal carbonyl techniques provided highly dispersed and fully sulfided intrazeolite Mo and Co sulfide clusters by use of Mo(CO)(6) and Co(CO)(3)NO, respectively. The Mo sulfide catalysts encaged in NaY exhibited much higher HDS activities than the impregnation catalysts. Go-Mo binary sulfide clusters were successfully synthesized in the pores of NaY as evidenced by EXAFS and XPS. The Co sites of the clusters were found to play important roles in hydrogenation and HDS. Thermally stable and catalytically active binary sulfide clusters for HDS are proposed to be intrazeolite Co2Mo2S6 molecular clusters. It was demonstrated that catalytic synergy between Co and Mo sulfides was generated by Co-S-Mo chemical bond formations. (C) 1997 Elsevier Science B.V.
引用
收藏
页码:45 / 59
页数:15
相关论文
共 80 条
[11]   FUNDAMENTAL-STUDIES OF TRANSITION-METAL SULFIDE HYDRODESULFURIZATION CATALYSTS [J].
CHIANELLI, RR .
CATALYSIS REVIEWS-SCIENCE AND ENGINEERING, 1984, 26 (3-4) :361-393
[12]   Fundamental studies of transition-metal sulfide catalytic materials [J].
Chianelli, RR ;
Daage, M ;
Ledoux, MJ .
ADVANCES IN CATALYSIS, VOL 40, 1994, 40 :177-232
[13]   SURFACE AND CATALYTIC PROPERTIES OF ALUMINA-SUPPORTED, SILICA-SUPPORTED, AND NAY ZEOLITE-SUPPORTED COMO CATALYSTS [J].
CID, R ;
VILLASENOR, J ;
ORELLANA, F ;
FIERRO, JLG ;
AGUDO, AL .
APPLIED CATALYSIS, 1985, 18 (02) :357-372
[14]   EFFECT OF COBALT ON STABILITY AND HYDRODESULFURIZATION ACTIVITY OF MOLYBDENUM CONTAINING Y-ZEOLITES [J].
CID, R ;
ORELLANA, F ;
AGUDO, AL .
APPLIED CATALYSIS, 1987, 32 (1-2) :327-336
[15]   PHYSICOCHEMICAL CHARACTERIZATION OF MOO3-NAY ZEOLITE CATALYSTS [J].
CID, R ;
LLAMBIAS, FJG ;
FIERRO, JLG ;
AGUDO, AL ;
VILLASENOR, J .
JOURNAL OF CATALYSIS, 1984, 89 (02) :478-488
[16]   SPILLOVER IN HETEROGENEOUS CATALYSIS [J].
CONNER, WC ;
FALCONER, JL .
CHEMICAL REVIEWS, 1995, 95 (03) :759-788
[17]   HYDROCRACKING OF VACUUM GAS-OIL ON THE NOVEL MESOPOROUS MCM-41 ALUMINOSILICATE CATALYST [J].
CORMA, A ;
MARTINEZ, A ;
MARTINEZSORIA, V ;
MONTON, JB .
JOURNAL OF CATALYSIS, 1995, 153 (01) :25-31
[18]   CHARACTERIZATION OF XMOO3.YNIO/USHY ZEOLITES BY IR, XPS, EXAFS, AND CATALYTIC HDS OF THIOPHENE - THE INFLUENCE OF METAL LOADING AND PREPARATION PROCEDURE [J].
CORMA, A ;
VAZQUEZ, MI ;
BIANCONI, A ;
CLOZZA, A ;
GARCIA, J ;
PALLOTA, O ;
CRUZ, JM .
ZEOLITES, 1988, 8 (06) :464-471
[19]  
CUI J, 1996, P 11 INT ZEOL C
[20]   CATALYTIC PROPERTIES OF MOLYBDENUM ZEOLITES IN EPOXIDATION REACTIONS .2. OXIDATION OF CYCLOHEXENE [J].
DAI, PE ;
LUNSFORD, JH .
JOURNAL OF CATALYSIS, 1980, 64 (01) :184-199