Luminescent properties of Ca2MgSi2O7 phosphor activated by Eu2+, Dy3+ and Nd3+

被引:52
作者
Jiang, L
Chang, CK
Mao, DL
Feng, CL
机构
[1] Shanghai Jiao Tong Univ, Sch Mat Sci & Engn, State Key Lab Met Matrix Composites, Shanghai 200030, Peoples R China
[2] Chinese Acad Sci, Shanghai Inst Organ Chem, State Key Lab Bioorgan & Nat Prod Chem, Shanghai 200032, Peoples R China
基金
上海市自然科学基金;
关键词
luminescence; afterglow; phosphor; Rietveld refinement;
D O I
10.1016/j.optmat.2004.02.019
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Long lasting alkaline earth silicates, Ca2MgSi2O7:Eu,Dy,Nd was prepared under a reduction atmosphere through solid,late reaction. The obtained phosphor was characterized by means of X-ray diffraction (XRD) and photoluminescence spectrum (PLS). The crystal structure of Ca2MgSi2O7:Eu,Dy,Nd phosphor was refined by Rietveld analysis. The obtained Ca2MgSi2O7:Eu,Dy,Nd phosphor showed a yellow-green emission peaking at 518 nm, which is ascribed to the luminescent emission of the Eu2+ that occupied the octa-coordinated Ca2+ sites in the Ca2MgSi2O7 host. The electron affinity (ea) value for Eu2+ in [EuO8] was calculated to 1.9 eV. The decay profile and the emission spectrum indicated that when the value of Dy/Eu is increasing, there is a concentration quenching of Eu2+. (C) 2004 Elsevier B.V. All rights reserved.
引用
收藏
页码:51 / 55
页数:5
相关论文
共 9 条
[1]   The 5d level positions of the trivalent lanthanides in inorganic compounds [J].
Dorenbos, P .
JOURNAL OF LUMINESCENCE, 2000, 91 (3-4) :155-176
[2]  
Liang J.K., 1985, CHIN J STRUCT CHEM, V4, P241
[3]   Preparation of a new long afterglow blue-emitting Sr2MgSi2O7-based photoluminescent phosphor [J].
Lin, YH ;
Tang, ZL ;
Zhang, ZT ;
Wang, XX ;
Zhang, JY .
JOURNAL OF MATERIALS SCIENCE LETTERS, 2001, 20 (16) :1505-1506
[4]   Luminescent properties of a new long afterglow EU2+ and Dy3+ activated Ca3MgSi2O8 phosphor [J].
Lin, YH ;
Zhang, ZT ;
Tang, ZL ;
Wang, XX ;
Zhang, JY ;
Zheng, ZS .
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2001, 21 (05) :683-685
[5]   Luminescence of Eu2+- in silicate host lattices with alkaline earth ions in a row [J].
Poort, SHM ;
Reijnhoudt, HM ;
vanderKuip, HOT ;
Blasse, G .
JOURNAL OF ALLOYS AND COMPOUNDS, 1996, 241 (1-2) :75-81
[6]   LINE PROFILES OF NEUTRON POWDER-DIFFRACTION PEAKS FOR STRUCTURE REFINEMENT [J].
RIETVELD, HM .
ACTA CRYSTALLOGRAPHICA, 1967, 22 :151-&
[7]   Long-lasting afterglow characteristics of Eu, Dy codoped SrO-Al2O3 phosphor [J].
Takasaki, H ;
Tanabe, S ;
Hanada, T .
JOURNAL OF THE CERAMIC SOCIETY OF JAPAN, 1996, 104 (04) :322-326
[8]  
Uitert L. G. V., 1984, J LUMIN, V29, P1
[9]   Mechanism of long phosphorescence of SrAl2O4:Eu2+, Dy3+ and CaAl2O4:Eu2+, Nd3+ [J].
Yamamoto, H ;
Matsuzawa, T .
JOURNAL OF LUMINESCENCE, 1997, 72-4 :287-289