Preparation and characterization of carbon nanotubes/aluminum matrix composites

2024Al matrix composite reinforced with 1 wt.% carbon nanotubes (CNTs) was fabricated by cold isostatic pressing, followed hot extrusion techniques. The microstructure characteristics and the distribution of carbon nanotubes in the aluminum matrix were investigated. The mechanical properties of the composite were measured at room temperature. Experimental results showed that CNTs were distributed homogeneously in the composite, and the interfaces of Al-CNTs bonded well. The grain size of the matrix was as fine as 200 nm, and with a small amount of CNTs additions, the elastic modulus and the tensile strength were enhanced markedly over those of the 2024Al matrix fabricated under the same process. The reasons for the increments could be due to the extraordinary mechanical properties of CNTs, the bridging and pulling out role of CNTs in the A1 matrix composite. (c) 2006 Elsevier B.V. All rights reserved.