Investigation of surface microstructural modification during tensile deformation in polypropylene using atomic force microscopy and Raman spectroscopy

被引:11
作者
Dasari, A [1 ]
Perkins, RS
Duncan, SJ
Misra, RDK
机构
[1] Univ Louisiana, Dept Chem Engn, Lafayette, LA 70504 USA
[2] Univ Louisiana, Dept Chem, Lafayette, LA 70504 USA
[3] Basell Polyolefins, Milton Keynes MK1 1LZ, Bucks, England
关键词
D O I
10.1179/026708303225009418
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Surface microstructural modification during tensile deformation in polypropylenes has been studied by atomic force microscopy (AFM) operated in tapping mode and Raman spectroscopy. The atomic force micrographs revealed differences in microstructures of undeformed and deformed polypropylenes that were used to predict the deformation characteristics of the two polypropylenes, designated as PP-L and PP-R. The undeformed surface of the two polypropylenes was characterised by differences in arrangement of fibrils depending on their melt flow conditions. PP-L is a polymer with longer chains and with restricted flow, and PP-R has shorter chains obtained by controlled rheology. The microfibrils in undeformed PP-L bend, forming raised surface features of height similar to 10-50 nm, whereas microfibrils in undeformed PP-R exhibit surface features of relatively lower height (10-20 nm). 30 x 30 nm scan AFM images provided details of microfibrils containing chains of molecules of similar to0.5 nm wide. The large scan AFM micrographs of mechanically deformed PP-L and PP-R indicated that under identical conditions of tensile deformation, PP-R exhibits a very different deformed structure in comparison to PP-L. At low displacement rates of 7.5 cm min(-1), both PP-L and PP-R exhibited splitting of molecular chains. However at high displacement rates of 50 cm min(-1), splitting was absent in both. Raman spectroscopy provided an insight of the molecular deformation of polymeric materials. The observations indicated that the rate of shift of frequency of Raman band per percent strain is greater for PP-L and less for PP-R, implying that PP-L experiences higher molecular deformation in comparison to PP-R. It is possible that the shorter chains in PP-R are less likely to unravel and separate less easily than the longer chains in PP-L.
引用
收藏
页码:231 / 238
页数:8
相关论文
共 30 条
[1]  
ALBRECHT TR, 1999, POLYM SCI, V74, P2243
[2]   Multi-objective optimization in material design and selection [J].
Ashby, MF .
ACTA MATERIALIA, 2000, 48 (01) :359-369
[3]   Tapping mode and phase imaging of biaxially oriented polyester films [J].
Beake, BD ;
Leggett, GJ ;
Shipway, PH .
SURFACE AND INTERFACE ANALYSIS, 2001, 31 (01) :39-45
[4]   Scratching maps for polymers [J].
Briscoe, BJ ;
Evans, PD ;
Pelillo, E ;
Sinha, SK .
WEAR, 1996, 200 (1-2) :137-147
[5]   Scratch hardness and deformation maps for polycarbonate and polyethylene [J].
Briscoe, BJ ;
Pelillo, E ;
Sinha, SK .
POLYMER ENGINEERING AND SCIENCE, 1996, 36 (24) :2996-3005
[6]  
CHU J, 1998, P INT SAMPE S, V43, P1149
[7]   Microstructural aspects of tensile deformation of high density polyethylene [J].
Dasari, A ;
Duncan, SJ ;
Misra, RDK .
MATERIALS SCIENCE AND TECHNOLOGY, 2003, 19 (02) :244-252
[8]   Micro- and nanoscale evaluation of scratch damage in poly(propylene)s [J].
Dasari, A ;
Rohrmann, J ;
Misra, RDK .
MACROMOLECULAR MATERIALS AND ENGINEERING, 2002, 287 (12) :889-903
[9]   Atomic force microscopy of scratch damage in polypropylene [J].
Dasari, A ;
Duncan, SJ ;
Misra, RDK .
MATERIALS SCIENCE AND TECHNOLOGY, 2002, 18 (10) :1227-1234
[10]  
DASARI A, 2002, MAT SCI TECHNOL, V29, P685