Study on the crystallization process of Ni-P amorphous alloy

被引:67
作者
Li, HX
Chen, HY
Dong, SH
Yang, JS
Deng, JF [1 ]
机构
[1] Fudan Univ, Dept Chem, Shanghai 200433, Peoples R China
[2] Fudan Univ, Dept Phys, Shanghai 200433, Peoples R China
关键词
D O I
10.1016/S0169-4332(97)00379-6
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
The thin film of Ni-P amorphous alloy deposited on the p-type silicon slice was prepared by electroless plating, which was then crystallized by heating it at high temperature from 550 K to 610 K in nitrogen flow for 2 h. Its crystallization process was investigated by using ICP, XRD, XPS, TEM, SEM and STM. No significant changes in the composition and the electronic structure on the surface have been observed during the crystallization process. However the changes in the amorphous structure and the surface area as well as the surface morphology are observed, which are attributed to the deactivation of the amorphous alloy after annealing during the hydrogenation reactions, Experimental results also reveal that the diffusion of the component elements in the NI-P alloy is essential during the crystallization because various crystalline diffraction peaks corresponding to Ni and Ni3P are observed simultaneously on XRD patterns. Based on those results, some modifications have been described to improve the thermal stability of the amorphous alloy. (C) 1998 Elsevier Science B.V.
引用
收藏
页码:115 / 119
页数:5
相关论文
共 16 条
[11]  
Moulder J.F., 1995, HDB XRAY PHOTOELECTR
[12]   METHODS FOR PREPARATION OF CATALYTIC MATERIALS [J].
SCHWARZ, JA ;
CONTESCU, C ;
CONTESCU, A .
CHEMICAL REVIEWS, 1995, 95 (03) :477-510
[13]   THE PREPARATION OF NI-P ULTRAFINE AMORPHOUS ALLOY PARTICLES BY CHEMICAL-REDUCTION [J].
SHEN, JY ;
HU, Z ;
ZHANG, LF ;
LI, ZY ;
CHEN, Y .
APPLIED PHYSICS LETTERS, 1991, 59 (27) :3545-3546
[14]  
TIWARI R, 1995, J MATER SCI, V30, P486
[15]  
Wonterghem J. V., 1986, NATURE, V322, P622
[16]  
[No title captured]