Solid polymeric electrolyte of PVC-ENR-LiClO4

被引：32

作者：

Ahmad, A.

Rahman, M. Y. A. ^{[1
]}

Ali, M. L. M.

Hashim, H.

Kalam, F. A.

机构：

[1] Univ Tenaga Nas, Coll Engn, Kajang 43009, Selangor, Malaysia

[2] Univ Kebangsaan Malaysia, Fac Sci & Technol, Bangi 43600, Selangor, Malaysia

来源：

IONICS | 2007年 / 13卷 / 02期

关键词：

PVC-ENR-LiClO4; electron beam cross-linking; ionic conductivity; solution casting;

D O I：

10.1007/s11581-007-0074-2

中图分类号：

O64 [物理化学（理论化学）、化学物理学];

学科分类号：

070304 ; 081704 ;

摘要：

The ionic conductivity of PVC-ENR-LiClO4 (PVC, polyvinyl chloride; ENR, epoxidized natural rubber) as a function of LiClO4 concentration, ENR concentration, temperature, and radiation dose of electron beam crosslinking has been studied. The electrolyte samples were prepared by solution casting technique. Their ionic conductivities were measured using the impedance spectroscopy technique. It was observed that the relationship between the concentration of salt, as well as temperature, and conductivity were linear. The electrolyte conductivity increases with ENR concentration. This relationship was discussed using the number of charge carrier theory. The conductivity-temperature behaviour of the electrolyte is Arrhenian. The conductivity also varies with the radiation dose of the electron beam cross-linking. The highest room temperature conductivity of the electrolyte of 8.5 x 10(-7) S/cm was obtained at 30% by weight of LiClO4. The activation energy, Ea and pre-exponential factor, sigma(o), are 1.4 x 10(-2) eV and 1.5 x 10(-11) S/cm, respectively

引用

页码：67 / 70

页数：4

共 16 条

[11]

Rahman MYA, 2002, SOLID STATE IONICS: TRENDS IN THE NEW MILLENNIUM, PROCEEDINGS, P401

[12] Increased lithium-ion conductivity in (PEG)46LiClO4 solid polymer electrolyte with δ-Al2O3 nanoparticles [J].