Microstructure and heat-treatment response of Al-2024/TiC composites

被引:62
作者
Albiter, A
León, CA
Drew, RAL
Bedolla, E
机构
[1] McGill Univ, Dept Min & Met Engn, Montreal, PQ H3A 2B2, Canada
[2] UMSNH, Inst Invest Met, Morelia 58000, Michoacan, Mexico
来源
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2000年 / 289卷 / 1-2期
关键词
metal matrix composites; Al-2024; alloy; titanium carbide; heat treatment; microstructure; tensile properties;
D O I
10.1016/S0921-5093(00)00900-X
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
Composites of a commercial Al-2024 alloy reinforced with particulate TiC have been produced by the pressureless melt infiltration route. Infiltration was carried out at 1200 degrees C for 2 h and composite materials containing 52 and 55 vol.% TiC were obtained. The phases other than the matrix and the reinforcement were identified as CuAl2, AlTi3, Ti3AlC, and TiAl3. It was found that the composites were age hardenable after solutionizing at 530 degrees C for 150 min and subsequent natural or artificial ageing at 190 degrees C. Mechanical properties of the composites, as-fabricated and heat-treated, showed a strong dependency on the ceramic content. After heat treatment, the 55% TiC composites showed an increase of hardness from 28.5 to 38.5 HRC; meanwhile ultimate tensile strength increased from 379 to 480 MPa. A similar behavior, as a function of heat treatment, was observed for the composites containing 52% TiC, but the estimated values were lower than those obtained for the 55% TiC composites. Scanning electron microscope (SEM) examination revealed transgranular fracture throughout the CuAl2 agglomerated precipitates in the as-fabricated composites. In the heat-treated conditions, brittle and intergranular fractures were observed. (C) 2000 Elsevier Science S.A. All rights reserved.
引用
收藏
页码:109 / 115
页数:7
相关论文
共 19 条
[1]   DEVELOPMENT OF AL-TI-C GRAIN REFINERS CONTAINING TIC [J].
BANERJI, A ;
REIF, W .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1986, 17 (12) :2127-2137
[2]   Microstructures and age hardenability of Al-5%Si-0.2%Mg based composites reinforced with particulate SiC [J].
Cocen, U ;
Onel, K ;
Ozdemir, I .
COMPOSITES SCIENCE AND TECHNOLOGY, 1997, 57 (07) :801-808
[3]   Kinetic study of the infiltration of aluminum alloys into TiC preforms [J].
Contreras, A ;
Salazar, M ;
León, CA ;
Drew, RAL ;
Bedolla, E .
MATERIALS AND MANUFACTURING PROCESSES, 2000, 15 (02) :163-182
[4]  
Davis J., 1994, ALUMINUM ALUMINUM AL
[5]   DISCUSSION OF ON THE FREE-ENERGY OF FORMATION OF TIC AND AL4C3 [J].
FINE, ME ;
CONLEY, JG .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1990, 21 (09) :2609-2610
[6]  
FURUKAWA M, 1995, METALL MATER TRANS A, V26, P663
[7]   Effect of particulate type on the microstructure and heat-treatment response of Al-Cu-based metal-matrix composites [J].
Gupta, M ;
Qin, S ;
Chin, LW .
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 1997, 65 (1-3) :245-251
[8]   THE INFLUENCE OF MATRIX MICROSTRUCTURE AND PARTICLE REINFORCEMENT ON THE CREEP-BEHAVIOR OF 2219 ALUMINUM [J].
KRAJEWSKI, PE ;
ALLISON, JE ;
JONES, JW .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1993, 24 (12) :2731-2741
[9]   AN INVESTIGATION OF THE ROLE OF A LIQUID-PHASE IN AL-CU-MG METAL-MATRIX COMPOSITES EXHIBITING HIGH-STRAIN RATE SUPERPLASTICITY [J].
MABUCHI, M ;
HIGASHI, K ;
LANGDON, TG .
ACTA METALLURGICA ET MATERIALIA, 1994, 42 (05) :1739-1745
[10]   INFLUENCE OF DEFORMATION BEFORE ARTIFICIAL AGING ON PROPERTIES OF AL-CU-MG ALUMINUM-ALLOY [J].
MAZZINI, SG .
SCRIPTA METALLURGICA ET MATERIALIA, 1994, 31 (09) :1127-1130