Phase transformation and oxygen equilibration kinetics of pure and Zr-doped Ba0.5Sr0.5Co0.8Fe0.2O3-δ perovskite oxide probed by electrical conductivity relaxation

被引：67

作者：

Yakovlev, S.

Yoo, C. -Y.

Fang, S.

Bouwmeester, H. J. M. ^{[1
]}

机构：

[1] Univ Twente, Dept Sci & Technol, Membrane Technol Grp, IMPACT, NL-7500 AE Enschede, Netherlands

来源：

APPLIED PHYSICS LETTERS | 2010年 / 96卷 / 25期

关键词：

annealing; barium compounds; cobalt compounds; electrical conductivity; polymorphic transformations; strontium compounds; surface diffusion; zirconium; PERMEATION; MEMBRANE; EXCHANGE; PERFORMANCE; DIFFUSION; EXPANSION; STABILITY;

D O I：

10.1063/1.3455908

中图分类号：

O59 [应用物理学];

学科分类号：

摘要：

Electrical conductivity relaxation is used for monitoring the cubic-to-hexagonal phase transition in the perovskite-type oxide Ba0.5Sr0.5Co0.8Fe0.2O3-delta. After in situ annealing at 1173 K, at which temperature the cubic polymorph is stable, electrical conductivity relaxation experiments are conducted during long-term annealing at 1073 K. The decreases in the surface exchange and chemical diffusion coefficients with time due to the sluggish phase transition are found to be correlated. It is demonstrated that B-site doping with Zr to an amount as low as 3 mol % stabilizes the high-temperature perovskite cubic phase of Ba0.5Sr0.5Co0.8Fe0.2O3-delta, with preservation of its high oxygen transport and exchange properties. (C) 2010 American Institute of Physics. [doi:10.1063/1.3455908]