Mossbauer and magnetic study of substituted magnetites

Co, Ni, Mn, Cr, and Cu substituted magnetites were prepared by the hydrothermal method at 300 degrees C, with concentrations ranging from 8.2% to 12.5%. Transmission electron microscopy determined the average particle diameter (Phi) to be in the hundred of nm range and the morphological modifications induced by the various substitutions employed, Hysteresis loop measurements were performed to determine the coercive field H-c, and saturation magnetic moment m(s). While H-c decreased with increasing (Phi), the particle shape was found to play an important role in explaining the dependence of m(s) on (Phi). Transmission Mossbauer spectroscopy was used to determine the site preference of the substitutions and their effect on the hyperfine magnetic fields. The room-temperature Mossbauer spectra were analyzed assuming a random distribution of substitutents using the binomial distribution from the ionic crystal point of view. Superparamagnetic particles were observed at room temperature in the case of Cu and Cr substituted magnetites. (C) 1998 American Institute of Physics.