Interdiffusion and phase formation in Cu(Sn) alloy films

被引:32
作者
Clevenger, LA [1 ]
Arcot, B
Ziegler, W
Colgan, EG
Hong, QZ
d'Heurle, FM
Cabral, C
Gallo, TA
Harper, JME
机构
[1] IBM Corp, Div Res, TJ Watson Res Ctr, Yorktown Heights, NY 10598 USA
[2] KTH Electrum, S-16440 Kista, Sweden
关键词
D O I
10.1063/1.366728
中图分类号
O59 [应用物理学];
学科分类号
摘要
The interdiffusion of Cu and Sn, and the formation and dissolution of Cu-Sn precipitates have been examined for Cu alloy films. Cu(Sn) films were deposited by electron beam evaporation either as Sn/Cu bilayers or Cu/Sn/Cu trilayers, with overall Sn concentrations from 0.1 to 5 at. %. In situ resistance, calorimetry, electron, and x-ray diffraction measurements indicate that eta-Cu6Sn5 forms during film deposition. Upon heating, epsilon-Cu3Sn forms at 170 degrees C, then this phase dissolves into the Cu matrix at approximately 350 degrees C. Finally, zeta-Cu10Sn3 forms and precipitates after thermal cycling to 500 degrees C. The final resistivity of Cu/Sn/Cu films with more than 2 at. % Sn exceeds 3.5 mu Omega cm. However, resistivities from 1.9 to 2.5 mu Omega cm after annealing were reached in Cu/Sn/Cu films with less than 2 at. % Sn. Auger and Rutherford backscattering analysis of Cu/Sn bilayers (1 mm thick) showed that the homogenization of Sn in Cu requires annealing in excess of 350 degrees C for 30 min; after annealing, the Sn concentration at the surface is approximately 20 at. %. The interdiffusion of Sn and Cu is inhibited by contamination at the Sn/Cu interface caused by air exposure. (C) 1998 American Institute of Physics.
引用
收藏
页码:90 / 99
页数:10
相关论文
共 38 条
[1]   THIN-FILM GROWTH OF SN ON CU(100) [J].
ABEL, F ;
COHEN, C ;
DAVIES, JA ;
MOULIN, J ;
SCHMAUS, D .
APPLIED SURFACE SCIENCE, 1990, 44 (01) :17-27
[2]   INTERMETALLIC FORMATION IN COPPER/MAGNESIUM THIN-FILMS - KINETICS, NUCLEATION AND GROWTH, AND EFFECT OF INTERFACIAL OXYGEN [J].
ARCOT, B ;
MURARKA, SP ;
CLEVENGER, LA ;
HONG, QZ ;
ZIEGLER, W ;
HARPER, JME .
JOURNAL OF APPLIED PHYSICS, 1994, 76 (09) :5161-5170
[3]  
BUTRYMOWICZ DB, 1981, DIFFUSION RATE DAT 2, P398
[4]  
Cabane J., 1991, Diffusion and Defect Data - Solid State Data, Part B (Solid State Phenomena), V15-16, P1
[5]   PREPARATION OF LOW RESISTIVITY CU-1 AT PERCENT CR THIN-FILMS BY MAGNETRON SPUTTERING [J].
CABRAL, C ;
HARPER, JME ;
HOLLOWAY, K ;
SMITH, DA ;
SCHAD, RG .
JOURNAL OF VACUUM SCIENCE & TECHNOLOGY A-VACUUM SURFACES AND FILMS, 1992, 10 (04) :1706-1712
[6]   COMPARISON OF HIGH-VACUUM AND ULTRAHIGH-VACUUM TANTALUM DIFFUSION BARRIER PERFORMANCE AGAINST COPPER PENETRATION [J].
CLEVENGER, LA ;
BOJARCZUK, NA ;
HOLLOWAY, K ;
HARPER, JME ;
CABRAL, C ;
SCHAD, RG ;
CARDONE, F ;
STOLT, L .
JOURNAL OF APPLIED PHYSICS, 1993, 73 (01) :300-308
[7]  
Davis L. E, 1976, HDB AUGER ELECT SPEC
[8]  
dHeurle F.M., 1995, SOLID STATE PHENOM, V41, P93, DOI DOI 10.4028/WWW.SCIENTIFIC.NET/SSP.41.93
[9]   NUCLEATION OF A NEW PHASE FROM THE INTERACTION OF 2 ADJACENT PHASES - SOME SILICIDES [J].
DHEURLE, FM .
JOURNAL OF MATERIALS RESEARCH, 1988, 3 (01) :167-195
[10]   NUCLEATION OF NEW SOLID-PHASES FROM CHEMICAL INTERACTIONS AT AN INTERFACE [J].
DHEURLE, FM .
JOURNAL OF VACUUM SCIENCE & TECHNOLOGY A-VACUUM SURFACES AND FILMS, 1989, 7 (03) :1467-1471