A delamination mechanism for thermal barrier coatings subject to calcium-magnesium-alumino-silicate (CMAS) infiltration

被引:375
作者
Mercer, C
Faulhaber, S
Evans, AG
Darolia, R
机构
[1] Univ Calif Santa Barbara, Dept Mat, Santa Barbara, CA 93106 USA
[2] GE Transportat, Cincinnati, OH 45215 USA
关键词
coatings; delamination; scanning electron microscopy; residual stresses; calcium-magnesium-alumino-silicate;
D O I
10.1016/j.actamat.2004.11.028
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
When a turbine airfoil attains temperatures that allow calcium-magnesium-alumino-silicate (CMAS) infiltration into the thermal barrier coating (TBC), a new mechanism of in-service spalling may be activated. The mechanism is associated with cold shock of the infiltrated layer during shut down. It has been identified by inspecting an airfoil removed from service. The identification has been based on observations of sub-surface delaminations within infiltrated regions of the TBC. Three important aspects of the mechanism are as follows. (a) The sub-surface delaminations always initiate at surface-connected vertical separations. (b) They are fully-infiltrated with CMAS. (c) They are strictly mode I. A thermal shock analysis has been invoked to identify a critical infiltration thickness, above which delaminations are possible. The analysis also defines a characteristic depth beneath the surface at which the delaminations are most likely. The observations made on the airfoils are consistent with these two dimensions. A second mechanism has been explored as the potential cause of large spalled regions also observed on the airfoils. But it has not been possible to verify the mechanism using the current observations. (C) 2004 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
引用
收藏
页码:1029 / 1039
页数:11
相关论文
共 29 条
[11]   A numerical model for the cyclic instability of thermally grown oxides in thermal barrier systems [J].
Karlsson, AM ;
Evans, G .
ACTA MATERIALIA, 2001, 49 (10) :1793-1804
[12]   A model study of displacement instabilities during cyclic oxidation [J].
Karlsson, AM ;
Levi, CG ;
Evans, AG .
ACTA MATERIALIA, 2002, 50 (06) :1263-1273
[13]   DEPOSITION OF VOLCANIC MATERIALS IN THE HOT SECTIONS OF 2 GAS-TURBINE ENGINES [J].
KIM, J ;
DUNN, MG ;
BARAN, AJ ;
WADE, DP ;
TREMBA, EL .
JOURNAL OF ENGINEERING FOR GAS TURBINES AND POWER-TRANSACTIONS OF THE ASME, 1993, 115 (03) :641-651
[14]  
KRAMER S, 2004, IN PRESS THERMOCHEMI
[15]  
Maricocchi A., 1995, THERMAL BARRIER COAT, P79
[16]   OXIDATION-BASED MODEL FOR THERMAL BARRIER COATING LIFE [J].
MILLER, RA .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1984, 67 (08) :517-521
[17]  
MILLER RA, 1995, P THERM BARR COAT WO, P17
[18]   Characterization of a cyclic displacement instability for a thermally grown oxide in a thermal barrier system [J].
Mumm, DR ;
Evans, AG ;
Spitsberg, IT .
ACTA MATERIALIA, 2001, 49 (12) :2329-2340
[19]   Observation of subcritical spall propagation of a thermal barrier coating [J].
Sergo, V ;
Clarke, DR .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1998, 81 (12) :3237-3242
[20]  
SMIALEK JL, 1992, SAMPE, V3, pM63