Damage accumulation and fracture initiation in uncracked ductile solids subject to triaxial loading

被引：416

作者：

Xue, Liang ^{[1
]}

机构：

[1] MIT, Dept Mech Engn, Cambridge, MA 02139 USA

来源：

INTERNATIONAL JOURNAL OF SOLIDS AND STRUCTURES | 2007年 / 44卷 / 16期

关键词：

ductile fracture; hydrostatic pressure; lode dependence; damage plasticity model;

D O I：

10.1016/j.ijsolstr.2006.12.026

中图分类号：

O3 [力学];

学科分类号：

08 ; 0801 ;

摘要：

A damage plasticity model for ductile fracture is proposed. This model is established on the cylindrical coordinate system of principal stress space. Experimental results show that fracture initiation in uncracked ductile solids is sensitive to the hydrostatic pressure and dependent on the Lode angle. The joint effects of pressure and Lode angle define a fracture envelope in principal stress space. Plastic deformation induced damage is calculated by an integral of the damage rate measured at current loading and deformation status with respect to the fracture envelope. A power law damage rule is proposed to characterize the nonlinearity in damage accumulation. A damage-related weakening factor is adopted to describe the material deterioration. The material parameters are calibrated from standard laboratory tests. The proposed model is numerically implemented. Four simulations with emphasis on crack path prediction are presented. (c) 2006 Elsevier Ltd. All rights reserved.

引用

页码：5163 / 5181

页数：19

共 58 条

[11]

Coffin L.F., 1954, T AM SOC MECH ENG, V76, P931, DOI [10.1115/1.4015020, DOI 10.1115/1.4015020]

[12]

COFFIN LF, 1958, P S INT STRESS FAT M, P363

[13]

COFFIN LF, 1967, THERMAL HIGH STRAIN, P171

[14]

Dawicke DS, 1995, ASTM STP 1256 AM SOC, P223

[15] CONTINUUM THEORY OF DUCTILE RUPTURE BY VOID NUCLEATION AND GROWTH .1. YIELD CRITERIA AND FLOW RULES FOR POROUS DUCTILE MEDIA [J].

GURSON, AL .

JOURNAL OF ENGINEERING MATERIALS AND TECHNOLOGY-TRANSACTIONS OF THE ASME, 1977, 99 (01) :2-15

[16]

Halford GR., 1962, P AM SOC TEST MATER, V62, P695

[17] MECHANISMS OF DUCTILE FAILURE IN HIGH-STRENGTH STEELS SUBJECTED TO MULTI-AXIAL STRESS STATES [J].

HANCOCK, JW ;

MACKENZIE, AC .

JOURNAL OF THE MECHANICS AND PHYSICS OF SOLIDS, 1976, 24 (2-3) :147-&

[18] ON DISCONTINUOUS PLASTIC STATES, WITH SPECIAL REFERENCE TO LOCALIZED NECKING IN THIN SHEETS [J].

HILL, R .

JOURNAL OF THE MECHANICS AND PHYSICS OF SOLIDS, 1952, 1 (01) :19-30

[19] INFLUENCE OF STRESS TRIAXIALITY UPON DUCTILE CRACK-PROPAGATION [J].

HOLLAND, D ;

HALIM, A ;

DAHL, W .

STEEL RESEARCH, 1990, 61 (10) :504-506

[20] The effect of crack tunneling on crack growth: experiments and CTOA analyses [J].

James, MA ;

Newman, JC .

ENGINEERING FRACTURE MECHANICS, 2003, 70 (3-4) :457-468

← 1 2 3 4 5 6 →