Effect of nickel content on the sintering behavior, mechanical and dielectric properties of Al2O3/Ni composites from coated powders

被引:54
作者
Lu, JS [1 ]
Gao, L [1 ]
Sun, J [1 ]
Gui, LH [1 ]
Guo, JK [1 ]
机构
[1] Chinese Acad Sci, Shanghai Inst Ceram, State Key Lab High Performance Ceram & Superfine, Shanghai 200050, Peoples R China
来源
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2000年 / 293卷 / 1-2期
基金
中国国家自然科学基金; 中国博士后科学基金;
关键词
ceramic-metal composite; coated powder; sintering behavior; mechanical properties; dielectric properties;
D O I
10.1016/S0921-5093(00)01231-4
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
Al2O3/Ni composites were fabricated by hot pressing coated powders, in which nanosized Ni particles were coated with layers of alumina precursor by the heterogeneous precipitation method. The calcined powders could be sintered to above 96% of the theoretical density at as low temperature as 1350 degrees C. The average alumina grain size in the composites decreased with increasing Ni content. Compared with that of monolithic alumina, the fracture toughness and the fracture strength of alumina could be increased by 28 and 43% by adding 2 and 5.5 vol.% Ni, respectively. The enhancement in mechanical properties can be explained from the unique microstructure of sintered bodies. The dielectric constant of Al2O3/Ni composites was found to increase with Ni content, which should be primarily attributed to the size effect of alumina grains. (C) 2000 Elsevier Science S.A. All rights reserved.
引用
收藏
页码:223 / 228
页数:6
相关论文
共 20 条
[1]   SOL-GEL PREPARED NI-ALUMINA COMPOSITE-MATERIALS .1. MICROSTRUCTURE AND MECHANICAL-PROPERTIES [J].
BREVAL, E ;
DENG, Z ;
CHIOU, S ;
PANTANO, CG .
JOURNAL OF MATERIALS SCIENCE, 1992, 27 (06) :1464-1468
[2]   SOL-GEL PREPARED NI-ALUMINA COMPOSITE-MATERIALS .2. STRUCTURE AND HOT-PRESSING TEMPERATURE [J].
BREVAL, E ;
PANTANO, CG .
JOURNAL OF MATERIALS SCIENCE, 1992, 27 (20) :5463-5469
[3]   Preparation and applications of coated powders in ceramics and related fields [J].
Giesche, H .
JOURNAL OF DISPERSION SCIENCE AND TECHNOLOGY, 1998, 19 (2-3) :249-265
[4]   INFLUENCE OF A TANGENTIAL FORCE ON THE FRACTURE OF 2 CONTACTING ELASTIC BODIES [J].
CHIANG, SS ;
EVANS, AG .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1983, 66 (01) :4-10
[5]   Modifications to the Zener Formula for Limitation of Grain Size [J].
Haroun, N. A. ;
Budworth, D. W. .
JOURNAL OF MATERIALS SCIENCE, 1968, 3 (03) :326-328
[6]   Synthesis and thermal properties of ultrafine powders of iron group metals [J].
Lu, JS ;
Yang, HB ;
Yu, S ;
Zou, GT .
MATERIALS CHEMISTRY AND PHYSICS, 1996, 45 (03) :197-202
[7]   PROCESSING AND PROPERTIES OF PARTICULATE COMPOSITES FROM COATED POWDERS [J].
MITCHELL, TD ;
DEJONGHE, LC .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1995, 78 (01) :199-204
[8]   Characteristics of dielectric behavior in nanostructured materials [J].
Mo, CM ;
Zhang, LD ;
Wang, GZ .
NANOSTRUCTURED MATERIALS, 1995, 6 (5-8) :823-826
[9]  
MOUNTVALA AJ, 1970, ULTRAFINE GRAIN CERA, P367
[10]   FABRICATION AND MECHANICAL-BEHAVIOR OF AL2O3/MO NANOCOMPOSITES [J].
NAWA, M ;
SEKINO, T ;
NIIHARA, K .
JOURNAL OF MATERIALS SCIENCE, 1994, 29 (12) :3185-3192