Influence of the brazing parameters on microstructure, residual stresses and shear strength of diamond-metal joints

被引：70

作者：

Buhl, Sebastian ^{[1
,2
]}

Leinenbach, Christian ^{[2
]}

Spolenak, Ralph ^{[3
]}

Wegener, Konrad ^{[1
]}

机构：

[1] ETH, Inst Machine Tools & Mfg, CH-8092 Zurich, Switzerland

[2] EMPA Duebendorf, Lab Joining & Interface Technol, CH-8600 Dubendorf, Switzerland

[3] ETH, Lab Nanomet, CH-8093 Zurich, Switzerland

来源：

JOURNAL OF MATERIALS SCIENCE | 2010年 / 45卷 / 16期

关键词：

1ST-ORDER RAMAN MODE; MECHANICAL-PROPERTIES; UNIAXIAL-STRESS; OPTICAL PHONONS; CVD DIAMOND; PRESSURE; FILMS; ELASTICITY; DEPENDENCE; ADHESION;

D O I：

10.1007/s10853-010-4260-7

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The reliability and integrity of diamond cutting tools depend on the properties of diamond-metal joints as created by a brazing process. Block-shaped monocrystalline diamonds were brazed onto a steel substrate (X2CrNiMo 18-14-3), using silver-copper based Cusil-ABA (TM) (Ag-35wt%Cu-1.75wt%Ti) filler alloy. The experimental procedure includes a thorough microstructural investigation of the filler alloy, the determination of the induced residual stresses by Raman spectroscopy as well as the joint's shear strength utilizing a special shear device. The brazing processes were carried out at 850, 880 and 910 A degrees C for dwell durations of 10 and 30 min, respectively. At the steel interface two interlayers develop. The layers grow with extended dwell duration and higher brazing temperature. The residual stresses only slightly depend on the brazing parameters and exhibit a maximum value of -400 MPa. Unlike the residual stresses, the shear strength strongly depends on the brazing parameters and thus on the microstructure. Three failure modes could be identified; a ductile fracture in the filler alloy, a brittle fracture in the interlayers and a partly shattering of the diamond.

引用

页码：4358 / 4368

页数：11

共 46 条

[1]

Aleksandrov I.V., 1989, HIGH PRESSURE RES, V1, P333, DOI [10.1080/08957958908202491, DOI 10.1080/08957958908202491]

[2]

ALEKSANDROV IV, 1986, JETP LETT+, V44, P611

[3] EFFECT OF STATIC UNIAXIAL STRESS ON RAMAN SPECTRUM OF SILICON [J].

ANASTASSAKIS, E ;

PINCZUK, A ;

BURSTEIN, E ;

POLLAK, FH ;

CARDONA, M .

SOLID STATE COMMUNICATIONS, 1970, 8 (02) :133-+

[4] RAMAN-SPECTRA OF DIAMOND AT HIGH-PRESSURES [J].

BOPPART, H ;

VANSTRAATEN, J ;

SILVERA, IF .

PHYSICAL REVIEW B, 1985, 32 (02) :1423-1425

[5] High efficiency abrasive tool for honing [J].

Burkhard, G ;

Rehsteiner, F .

CIRP ANNALS-MANUFACTURING TECHNOLOGY, 2002, 51 (01) :271-274

[6] MICRO-RAMAN FOR DIAMOND FILM STRESS-ANALYSIS [J].

CHEN, KH ;

LAI, YL ;

LIN, JC ;

SONG, KJ ;

CHEN, LC ;

HUANG, CY .

[7] Elasticity of carbon allotropes. I. Optimization, and subsequent modification, of an anharmonic Keating model for cubic diamond [J].

Cousins, CSG .

PHYSICAL REVIEW B, 2003, 67 (02)

[8]

de Wolf I., 2003, Spectroscopy Europe, V15, P6

[9] Adhesion between CVD diamond and WC-Co induced by high-pressure and high-temperature [J].

dos Santos, S. I. ;

Balzaretti, N. M. ;

da Jornada, J. A. H. .

[10] Development and characterisation of Ag-Cu-Ti brazes prepared with planar flow casting [J].

Duhaj, P ;

Sebo, P ;

Svec, P ;

Janickovic, D .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1999, 271 (1-2) :181-187

← 1 2 3 4 5 →