Microvoltammetry for cathode materials at elevated temperatures: electrochemical stability of single particles

被引：66

作者：

Dokko, K ^{[1
]}

Horikoshi, S ^{[1
]}

Itoh, T ^{[1
]}

Nishizawa, M ^{[1
]}

Mohamedi, M ^{[1
]}

Uchida, I ^{[1
]}

机构：

[1] Tohoku Univ, Grad Sch Engn, Dept Appl Chem, Aoba Ku, Sendai, Miyagi 9808579, Japan

来源：

JOURNAL OF POWER SOURCES | 2000年 / 90卷 / 01期

关键词：

microelectrode; single particle; cycle stability; lithium ion battery; lithium manganese oxide; lithium cobalt oxide;

D O I：

10.1016/S0378-7753(00)00456-0

中图分类号：

O64 [物理化学（理论化学）、化学物理学];

学科分类号：

070304 ; 081704 ;

摘要：

The electrochemical stability of single particles of cathode materials (LiMn2O4, Li1.10Cr0.048Mn1.852O4, LiCoO2 and LiNi0.85Co0.15O2) was investigated by means of a microelectrode technique at 25 degrees C and 50 degrees C. The cycle stability was evaluated by multi-cyclic voltammetry. LiMn2O4 showed good cycle stability in LiClO4/propylene carbonate (PC) + ethylene carbonate (EC) and LiBF4/PC + EC solutions even at 50 degrees C. On the contrary, in LiPF6/PC + EC, significant capacity fading during charge-discharge was observed at 50 degrees C. The cycle stability of LiMn2O4 in the latter solution was improved by partial substitution of Mn by Cr and Li. Regarding LiCoO2, its cycle life in LiClO4/PC + EC at 50 degrees C was unsatisfactory when the potential was scanned between 3.60 and 4.30 V. On the other hand, LiCoO2 retained 90% of its capacity when the potential scan was limited to 4.00 V. LiNi0.85Co0.15O2 showed similar trend at 50 degrees C. (C) 2000 Elsevier Science S.A. All rights reserved.

引用

页码：109 / 115

页数：7

共 28 条

[21] PISOTOIA G, 1994, LITHIUM BATTERIES NE, V5
[22] ELECTROCHEMICAL AND INSITU X-RAY-DIFFRACTION STUDIES OF LITHIUM INTERCALATION IN LIXCOO2
REIMERS, JN
DAHN, JR
[J]. JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1992, 139 (08) : 2091 - 2097
[23] M3+-modified LiMn2O4 spinel intercalation cathodes .2. Electrochemical stabilization by Cr3+
Robertson, AD
Lu, SH
Howard, WF
[J]. JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1997, 144 (10) : 3505 - 3512
[24] Microvoltammetric studies on single particles of battery active materials
Uchida, I
Fujiyoshi, H
Waki, S
[J]. JOURNAL OF POWER SOURCES, 1997, 68 (01) : 139 - 144
[25] ELECTROCHEMICAL MEASUREMENTS OF SINGLE PARTICLES OF PD AND LANI5 WITH A MICROELECTRODE TECHNIQUE
URA, H
NISHINA, T
UCHIDA, I
[J]. JOURNAL OF ELECTROANALYTICAL CHEMISTRY, 1995, 396 (1-2): : 169 - 173
[26] Microvoltammetric studies on single particle voltammetry of LiNiO2 and LiCoO2. In situ observation of particle splitting during Li-ion extraction/insertion
Waki, S
Dokko, K
Matsue, T
Uchida, I
[J]. DENKI KAGAKU, 1997, 65 (11): : 954 - 962
[27] TEM study of electrochemical cycling-induced damage and disorder in LiCoO2 cathodes for rechargeable lithium batteries
Wang, HF
Jang, YI
Huang, BY
Sadoway, DR
Chiang, YT
[J]. JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1999, 146 (02) : 473 - 480
[28] Capacity fading on cycling of 4 V Li/LiMn2O4 cells
Xia, YY
Zhou, YH
Yoshio, M
[J]. JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1997, 144 (08) : 2593 - 2600

← 1 2 3 →