Preparation and characterization of Fe3O4(111) nanoparticles and thin films on Au(111)

被引：48

作者：

Deng, Xingyi ^{[1
]}

Lee, Junseok ^{[1
]}

Matranga, Christopher ^{[1
]}

机构：

[1] US DOE, NETL, Pittsburgh, PA 15236 USA

来源：

SURFACE SCIENCE | 2010年 / 604卷 / 7-8期

关键词：

Iron-oxides; Fe3O4(111); alpha-Fe2O3(0001); Nanoparticles and thin films; Au(111); Scanning tunneling microscopy (STM); X-ray photoelectron spectroscopy (XPS); IRON-OXIDE FILMS; GROWTH; SURFACE; FEO; NUCLEATION; CATALYST; OXYGEN;

D O I：

10.1016/j.susc.2010.01.006

中图分类号：

O64 [物理化学（理论化学）、化学物理学];

学科分类号：

070304 ; 081704 ;

摘要：

Fe3O4 nanoparticles and thin films were prepared on the Au(111) surface and characterized using X-ray photoelectron spectroscopy (XPS) and scanning tunneling microscopy (STM). Fe3O4 was formed by annealing alpha-Fe2O3(0001) structures on Au(111) at 750 K in ultrahigh vacuum (UHV) for 60 min. Transformation of the alpha-Fe2O3(0001) structures into Fe3O4 nanoparticles and thin films was supported by XPS. STM images show that during the growth procedure used, Fe3O4 initially appears as nanoparticles at low coverages, and forms thin films at similar to 2 monolayer equivalents (MLE) of iron. Two types of ordered superstructures were observed on the Fe3O4 particles with periodicities of similar to 50 and similar to 42 angstrom, respectively. As the Fe3O4 particles form more continuous films, the similar to 50 angstrom feature was the predominant superstructure observed. The Fe3O4 structures at all coverages show a hexagonal unit cell with a similar to 3 angstrom periodicity in the atomically resolved STM images. (C) 2010 Elsevier B.V. All rights reserved.