COLLOIDAL PROCESSING FOR LAMINATED COMPOSITES OF MULLITE ALUMINA WOVEN FABRICS

被引：2

作者：

HIRATA, Y

TAKESHIMA, K

机构：

[1] Department of Applied Chemistry and Chemical Engineering, Faculty of Engineering, Kagoshima University, Kagoshima, 890

来源：

MATERIALS LETTERS | 1993年 / 17卷 / 3-4期

关键词：

D O I：

10.1016/0167-577X(93)90070-E

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

A sol-gel-processed mullite powder and alumina woven fabrics were for-med into laminated composites (5 vol% alumina fabrics) by filtration of the aqueous mullite suspensions containing polyacrylic ammonium at pH = 8.8 which were poured into the spaces separated with alumina fabrics. The mullite suspensions with 30-55 vol% solids showed a Newtonian flow and formed high-density green compacts of 60-63% of the theoretical density (TD). The green composites were densified to near full density by hot-pressing at 1650-degrees-C for 1 h at 39 MPa in N2 atmosphere. The mechanical properties (strength, hardness and fracture toughness) of the dense composites (> 99% TD) were measured at room temperature. However, no significant improvements of strength and fracture toughness were obtained due to the formation of large cracks (> 100 mum) across the alumina fabrics and disappearance of long fiber characteristics after sintering.

引用

页码：125 / 130

页数：6

共 32 条

[11] Effects of addition of polyacrylic ammonium on colloidal processing of α-alumina [J].

Hirata, Yoshihiro ;

Nishimoto, Akihiko ;

Ishihara, Yoshimi .

Nippon Seramikkusu Kyokai Gakujutsu Ronbunshi/Journal of the Ceramic Society of Japan, 1992, 100 (1164) :983-990

[12]

HIRATA Y, 1992, NIPPON SERAM KYO GAK, V100, P353, DOI 10.2109/jcersj.100.353

[13]

ISMAIL MGMU, 1987, J AM CERAM SOC, V70, pC7, DOI 10.1111/j.1151-2916.1987.tb04857.x

[14]

JAKUS K, 1989, CERAM ENG SCI P, V10, P1338

[15]

KANZAKI S, 1985, J AM CERAM SOC, V68, pC6, DOI 10.1111/j.1151-2916.1985.tb15252.x

[16]

KATSUKI H, 1989, NIPPON SERAM KYO GAK, V97, P1521, DOI 10.2109/jcersj.97.1521

[17]

KERANS RJ, 1989, AM CERAM SOC BULL, V68, P429

[18]

KO FK, 1989, AM CERAM SOC BULL, V68, P401

[19]

Krnrazawa I., 1988, J CERAM SOC JPN, P85

[20]

LI JX, 1992, NIPPON SERAM KYO GAK, V100, P499, DOI 10.2109/jcersj.100.499

← 1 2 3 4 →