Young's modulus of nanocrystalline Fe measured by nanoindentation

被引:130
作者
Fougere, GE
Riester, L
Ferber, M
Weertman, JR
Siegel, RW
机构
[1] NORTHWESTERN UNIV, DEPT MAT SCI & ENGN, EVANSTON, IL 60208 USA
[2] OAK RIDGE NATL LAB, HIGH TEMP MAT LAB, OAK RIDGE, TN 37831 USA
[3] ARGONNE NATL LAB, DIV MAT SCI, ARGONNE, IL 60439 USA
来源
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 1995年 / 204卷 / 1-2期
关键词
Young's modulus; nanoindentation; iron;
D O I
10.1016/0921-5093(95)09927-1
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
Nanoindentation techniques were used to measure Young's modulus for nanocrystalline Fe samples produced by inert-gas condensation and warm consolidation. The samples had grain sizes of 4-20 nm and residual porosity of 2-30% calculated relative to conventional Fe. Values of Young's modulus for the nanocrystalline Fe are reduced relative to that of conventional, fully dense Fe. A review of Young's modulus for other nanocrystalline materials showed similar trends. Published results for porous conventional Fe showed similar reductions in Young's modulus for samples with comparable porosity levels. The observed reductions in Young's modulus for both the nanocrystalline and the conventional porous Fe can be described adequately by several theories utilizing spheroidal porosity.
引用
收藏
页码:1 / 6
页数:6
相关论文
共 27 条
[1]  
Boccaccini A.R., 1993, J MECH BEHAV MATER, V4, P119, DOI [10.1515/JMBM.1993.4.2.119, DOI 10.1515/JMBM.1993.4.2.119]
[2]   A method for interpreting the data from depth-sensing indentation instruments [J].
Doerner, M. F. ;
Nix, W. D. .
JOURNAL OF MATERIALS RESEARCH, 1986, 1 (04) :601-609
[3]   PROCESSING AND MECHANICAL-BEHAVIOR OF NANOCRYSTALLINE FE [J].
FOUGERE, GE ;
WEERTMAN, JR ;
SIEGEL, RW .
NANOSTRUCTURED MATERIALS, 1995, 5 (02) :127-134
[4]  
FOUGERE GE, 1995, THESIS NW U
[6]   EFFECT OF POROSITY ON YOUNG MODULUS OF ALUMINA [J].
KNUDSEN, FP .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1962, 45 (02) :94-95
[7]  
Kobelev N. P., 1993, Nanostructured Materials, V2, P537, DOI 10.1016/0965-9773(93)90171-7
[8]   MEASUREMENTS OF THE ELASTIC-CONSTANTS, THE SPECIFIC-HEAT AND THE ENTROPY OF GRAIN-BOUNDARIES BY MEANS OF ULTRA-FINE GRAINED MATERIALS [J].
KORN, D ;
MORSCH, A ;
BIRRINGER, R ;
ARNOLD, W ;
GLEITER, H .
JOURNAL DE PHYSIQUE, 1988, 49 (C-5) :769-779
[9]  
KRST, 1988, UIM, V23, P4097
[10]   EFFECT OF POROSITY ON YOUNG MODULUS OF NANOCRYSTALLINE MATERIALS [J].
KRSTIC, V ;
ERB, U ;
PALUMBO, G .
SCRIPTA METALLURGICA ET MATERIALIA, 1993, 29 (11) :1501-1504