EFFECT OF MICROSTRUCTURE ON STRESS-CORROSION CRACKING OF ALLOY 600 IN HIGH-PURITY WATER

被引：36

作者：

DOMIAN, HA

EMANUELSON, RH

SARVER, LW

THEUS, GJ

KATZ, L

机构：

[1] BABCOCK & WILCOX CO,ALLIANCE,OH 44601

[2] BABCOCK & WILCOX,BARBERTON,OH

来源：

CORROSION | 1977年 / 33卷 / 01期

关键词：

CORROSION - Stress Corrosion Cracking - NICKEL METALLOGRAPHY - Microstructures;

D O I：

10.5006/0010-9312-33.1.26

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Laboratory thermal-mechanical processing was used to produce Alloy 600 material with varying microstructures. The materials were fabricated into single U-band specimens and tested in 343 C (650 F) ammonia-hydrazine treated water for over 18,000 hours. Specimens exhibiting significant intergranular carbide precipitation were generally much more resistant to cracking than those that displayed less intergranular carbides. The results of microanalyses of cracked and uncracked specimens are presented, and the influence of various microstructural features are given.

引用

页码：26 / 37

页数：12

共 37 条

[11]

CORIOU H, 1969, 1967 P C FUND ASP ST

[12]

Coriou H., 1959, 3RD MET C CORR SACL, P161

[13]

CORIOUS H, 1972, IND ATOMIQUE SPATIAL, V2, P2

[14]

FLETCHER WD, 1975, SEP ANS AIME INT C M

[15]

FOSTER GG, 1971, EFFECTS ENVIRONMENT, P87

[16] INTERCRYSTALLINE STRESS CORROSION CRACKING OF INCONEL 600 INSPECTION TUBES IN AGESTA REACTOR [J].

GRONWALL, B ;

LJUNGBER.L ;

HUBNER, W ;

STURART, W .

NUCLEAR ENGINEERING AND DESIGN, 1967, 6 (04) :383-&

[17]

HEISE M, 1975, 165TH CEFA CEM NUCL

[18]

HUBNER W, 1972, 4TH P INT C MET CORR

[19]

HUBNER W, 1972, AEMK304

[20]

LATANISION RM, 1969, 1967 P C FUND ASP ST

← 1 2 3 4 →