HARDNESS OF 12CR-8MO FERRITIC STEELS IRRADIATED BY NI IONS

被引:15
作者
OHTA, J [1 ]
OHMURA, T [1 ]
KAKO, K [1 ]
TOKIWAI, M [1 ]
SUZUKI, T [1 ]
机构
[1] ELECT POWER IND, CENT RES INST, KOMAE, TOKYO 201, JAPAN
关键词
D O I
10.1016/0022-3115(95)00016-X
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
12Cr-8Mo and 12Cr-8Mo-0.1Y(2)O(3) ferritic steels were irradiated with 4-MeV Ni3+ ions up to 300 dpa at 525 degrees C. Microstructural evolution was examined by transmission electron microscopy (TEM) and mechanical properties were evaluated with a depth-sensing ultra-low load indentation hardness tester at room temperature with a maximum load of 1 gf. Effects of aging at 650 degrees C for 115 h and heat treatment at 525 degrees C for 50 h were also investigated. TEM observations reveal that these steels exhibit no void swelling in the present irradiation condition. Aging and heat treatment induces precipitation of Laves phase and ion-irradiation enhances precipitation. The induction and enhancement of precipitation strengthened the specimens.
引用
收藏
页码:187 / 191
页数:5
相关论文
共 28 条
[1]  
BAGLEY KO, 1987, MATERIALS NUCLEAR RE, V2, P37
[2]  
DAVIS JW, 1984, J NUCL MATER, V122, P51
[3]   A method for interpreting the data from depth-sensing indentation instruments [J].
Doerner, M. F. ;
Nix, W. D. .
JOURNAL OF MATERIALS RESEARCH, 1986, 1 (04) :601-609
[4]  
DUBISSON P, 1993, J NUCL MATER, V205, P178
[5]  
FARRELL K, 1985, ASTM STP, V870, P383
[6]   SWELLING IN SEVERAL COMMERCIAL ALLOYS IRRADIATED TO VERY HIGH NEUTRON FLUENCE [J].
GELLES, DS .
JOURNAL OF NUCLEAR MATERIALS, 1984, 122 (1-3) :207-213
[7]   MICROSTRUCTURAL EXAMINATION OF SEVERAL COMMERCIAL ALLOYS NEUTRON-IRRADIATED TO 100 DPA [J].
GELLES, DS .
JOURNAL OF NUCLEAR MATERIALS, 1987, 148 (02) :136-144
[8]  
GELLES DS, 1981, J NUCL MATER, V103, P975
[9]  
GILBON D, 1989, ASTM STP, V1046, P5
[10]   FATIGUE BEHAVIOR OF IRRADIATED HELIUM-CONTAINING FERRITIC STEELS FOR FUSION-REACTOR APPLICATIONS [J].
GROSSBECK, ML ;
VITEK, JM ;
LIU, KC .
JOURNAL OF NUCLEAR MATERIALS, 1986, 141 (pt B) :966-972