POLY(VINYLSILANE) - A PRECURSOR TO SILICON-CARBIDE .1. PREPARATION AND CHARACTERIZATION

被引:76
作者
BOURY, B [1 ]
CORRIU, RJP [1 ]
LECLERCQ, D [1 ]
MUTIN, PH [1 ]
PLANEIX, JM [1 ]
VIOUX, A [1 ]
机构
[1] UNIV MONTPELLIER 2,RHONE POULENC,CNRS,UM 44,PL E BATAILLON,F-34095 MONTPELLIER 05,FRANCE
关键词
D O I
10.1021/om00051a043
中图分类号
O61 [无机化学];
学科分类号
070301 ; 081704 ;
摘要
Poly(vinylsilane), (H2SiC2H4)n, has been synthesized by a hydrosilylation route. Depending on the experimental conditions, the average molecular weight varies from 640 to 5500. The structure of these polymers, which was investigated by H-1, C-13, and Si-29 NMR spectroscopy, is explained on the basis of the two possible modes of addition in the hydrosilylation reaction. Pyrolysis of either low or high molecular weight polymers gives similar ceramic yields (32-40%), which are higher than for non-cross-linked poly-(silapropylene), (CH3SiHCH2)n. This result emphasizes the role of the latent SiH functions in the pyrolysis step.
引用
收藏
页码:1457 / 1461
页数:5
相关论文
共 21 条
[1]  
Anderson D. R., 1974, ANAL SILICONES
[2]   NEW POLYCARBOSILANE MODELS .2. 1ST SYNTHESIS OF POLYSILAPROPYLENE [J].
BACQUE, E ;
PILLOT, JP ;
BIROT, M ;
DUNOGUES, J .
MACROMOLECULES, 1988, 21 (01) :34-38
[3]  
BOURY B, 1990, NEW J CHEM, V14, P535
[6]  
CURRY JW, 1958, J AM CHEM SOC, V80, P391
[7]   SYNTHESIS OF CONTINUOUS SILICON-CARBIDE FIBER .2. CONVERSION OF POLYCARBOSILANE FIBER INTO SILICON-CARBIDE FIBERS [J].
HASEGAWA, Y ;
IIMURA, M ;
YAJIMA, S .
JOURNAL OF MATERIALS SCIENCE, 1980, 15 (03) :720-728
[8]   SYNTHESIS OF CONTINUOUS SILICON-CARBIDE FIBER .4. THE STRUCTURE OF POLYCARBOSILANE AS THE PRECURSOR [J].
HASEGAWA, Y ;
OKAMURA, K .
JOURNAL OF MATERIALS SCIENCE, 1986, 21 (01) :321-328
[9]   THE PREPARATION OF VINYL AND ALLYL CHLOROSILANES [J].
HURD, DT .
JOURNAL OF THE AMERICAN CHEMICAL SOCIETY, 1945, 67 (10) :1813-1814
[10]  
KOBRAKOV KI, 1970, DOKL AKAD NAUK SSSR+, V191, P607