FRACTURE AND ACOUSTIC-EMISSION CHARACTERISTICS OF GLASS-FIBER-REINFORCED PLASTICS PANELS FOR HOT-WATER

This study deals with the fracture process and acoustic emission (AE) characteristics of a randomly oriented E-glass fiber mat reinforcement with a crosslinked polyester. These panels were evaluated after they were immersed in hot water. The fiber volume content of the panel was 19%. Glass fiber reinforced plastics (GFRP) panels were immersed in water at 80-degrees-C. Bending and AE monitoring tests were performed and after bending, the cross-section of the specimen was observed by an optical microscope and SEM. The influence of degradation, due to water immersion, on the changes of fracture process of GFRP is discussed. The dominant fracture mode of the virgin specimen was matrix cracks, whereas that of the immersed specimen was debondings at the fiber bundle/matrix and fiber/matrix interfaces. This change was caused by reduction of the bonding strength at the interface. The scale of fracture can be estimated by both AE amplitude and AE energy and this estimation method was used to estimate the fracture mode changes of GFRP panels immersed in hot water.