EFFECT OF HEAT-TREATMENT AND HEAT-TO-HEAT VARIATIONS IN THE FATIGUE-CRACK GROWTH-RESPONSE OF ALLOY 718

被引：44

作者：

JAMES, LA

MILLS, WJ

机构：

[1] Westinghouse Hanford Co, Richland,, WA, USA, Westinghouse Hanford Co, Richland, WA, USA

来源：

ENGINEERING FRACTURE MECHANICS | 1985年 / 22卷 / 05期

关键词：

CORROSION RESISTANCE - CREEP RESISTANCE - FRACTOGRAPHIC EXAMINATIONS - MICROSTRUCTURAL FACTORS - NICKEL-BASE SUPERALLOY;

D O I：

10.1016/0013-7944(85)90109-2

中图分类号：

O3 [力学];

学科分类号：

08 ; 0801 ;

摘要：

The fatigue-crack growth behavior of seven heats of Alloy 718 was studied at five different test temperatures. These seven heats represented at least four different producers, four were tested in two different heat-treated conditions. Heat-to-heat variations were noted; these were most obvious in material given the conventional heat-treatment. Electron fractographic examination revealed that operative crack growth mechanisms were dependent on heat treatment, heat-to-heat variations, test temperature and prevailing crack-tip stress-intensity level.

引用

页码：797 / 817

页数：21

共 28 条

[1]

BATES RC, 1969, T ASM, V62, P380

[2]

CLARK WG, 1975, J TEST EVAL, V3, P454, DOI 10.1520/JTE11702J

[3] FREQUENCY AND WAVE-FORM EFFECTS ON FATIGUE CRACK GROWTH-BEHAVIOR OF ALLOY 718 AT 298-K AND 823-K [J].

CLAVEL, M ;

PINEAU, A .

METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1978, 9 (04) :471-480

[4]

DURQUETTE DJ, 1971, METALL T, V2, P1325

[5] CHARACTERISTICS OF STAGE I FATIGUE FRACTURE IN A HIGH-STRENGTH NICKEL ALLOY [J].

GELL, M ;

LEVERANT, GR .

ACTA METALLURGICA, 1968, 16 (04) :553-&

[6]

GELL M, 1969, 2 P INT C FRACT, P565

[7]

HILL KA, 1973, THESIS LEHIGH U

[8] FATIGUE CRACK-PROPAGATION AT ELEVATED-TEMPERATURES IN SOLID-SOLUTION STRENGTHENED SUPER-ALLOYS [J].

JABLONSKI, DA ;

CARISELLA, JV ;

PELLOUX, RM .

METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1977, 8 (12) :1893-1900

[9]

JAMES LA, 1978, WELD J, V57, pS17

[10] EFFECT OF TEMPERATURE UPON FATIGUE-CRACK GROWTH BEHAVIOR OF 2 NICKEL-BASE ALLOYS [J].

JAMES, LA .

JOURNAL OF ENGINEERING MATERIALS AND TECHNOLOGY-TRANSACTIONS OF THE ASME, 1973, 95 (04) :254-256

← 1 2 3 →