EFFECT OF HEAT-TREATMENT AND HEAT-TO-HEAT VARIATIONS IN THE FATIGUE-CRACK GROWTH-RESPONSE OF ALLOY 718

被引：44

作者：

JAMES, LA

MILLS, WJ

机构：

[1] Westinghouse Hanford Co, Richland,, WA, USA, Westinghouse Hanford Co, Richland, WA, USA

来源：

ENGINEERING FRACTURE MECHANICS | 1985年 / 22卷 / 05期

关键词：

CORROSION RESISTANCE - CREEP RESISTANCE - FRACTOGRAPHIC EXAMINATIONS - MICROSTRUCTURAL FACTORS - NICKEL-BASE SUPERALLOY;

D O I：

10.1016/0013-7944(85)90109-2

中图分类号：

O3 [力学];

学科分类号：

08 ; 0801 ;

摘要：

The fatigue-crack growth behavior of seven heats of Alloy 718 was studied at five different test temperatures. These seven heats represented at least four different producers, four were tested in two different heat-treated conditions. Heat-to-heat variations were noted; these were most obvious in material given the conventional heat-treatment. Electron fractographic examination revealed that operative crack growth mechanisms were dependent on heat treatment, heat-to-heat variations, test temperature and prevailing crack-tip stress-intensity level.

引用

页码：797 / 817

页数：21

共 28 条

[11] THE EFFECT OF PRODUCT FORM UPON FATIGUE-CRACK GROWTH-BEHAVIOR IN ALLOY 718 [J].

JAMES, LA .

JOURNAL OF ENGINEERING MATERIALS AND TECHNOLOGY-TRANSACTIONS OF THE ASME, 1981, 103 (03) :234-239

[12]

JAMES LA, 1979, ASTM STP679 AM SOC T, P3

[13]

JAMES LA, 1975, HEDLTME7580 WEST HAN

[14]

LOGSDON WA, 1977, 779E7CRYMTP2 WEST RE

[15] ON FATIGUE CRACK PROPAGATION IN FCC METALS [J].

MCEVILY, AJ ;

BOETTNER, RC .

ACTA METALLURGICA, 1963, 11 (07) :725-&

[16] EFFECT OF TEMPERATURE ON THE FATIGUE-CRACK PROPAGATION BEHAVIOR OF INCONEL X-750 [J].

MILLS, WJ ;

JAMES, LA .

FATIGUE OF ENGINEERING MATERIALS AND STRUCTURES, 1980, 3 (02) :159-175

[17]

MILLS WJ, 1975, FATIGUE COMPOSITE MA, P5

[18]

MILLS WJ, 1978, HEDLTME7854 WEST HAN

[19]

MILLS WJ, 1978, ASME78WAPVP3 PAP

[20]

MOON DM, 1973, ASTM STP, V520, P438

← 1 2 3 →