EFFECTS OF AGING ON THE GAS-PERMEABILITY AND SOLUBILITY IN POLY(1-TRIMETHYLSILYL-1-PROPYNE) MEMBRANES SYNTHESIZED WITH VARIOUS CATALYSTS

被引：110

作者：

NAGAI, K ^{[1
]}

NAKAGAWA, T ^{[1
]}

机构：

[1] MEIJI UNIV,DEPT IND CHEM,TAMA KU,KAWASAKI,KANAGAWA 214,JAPAN

来源：

JOURNAL OF MEMBRANE SCIENCE | 1995年 / 105卷 / 03期

关键词：

POLY (1-TRIMETHYLSILYL-1-PROPYNE); GAS PERMEABILITY; AGING; MEMBRANE CONTAMINATION; VACUUM PUMP OIL VAPOR;

D O I：

10.1016/0376-7388(95)00065-K

中图分类号：

TQ [化学工业];

学科分类号：

0817 ;

摘要：

The effects of aging on the gas permeability and solubility in glassy poly(1-trimethylsilyl-1-propyne) (PMSP) membranes were investigated in terms of polymer characterization and storage environment. Under the aging conditions in the presence of vacuum pump oil vapor, in which a very small amount of vacuum pump oil vapor sorbed in the PMSP membrane served as an accelerator of physical aging rather than as a filler, the aging of the gas permeability of the PMSP membranes was dependent on their thickness, the polymerization catalyst and molecular weight. On the other hand, catalyst dependence on the gas permeability was not observed during annealing. Additionally, the aging of the gas sorption in the PMSP membranes was similar to that of the gas permeability. Storage in liquid nitrogen and exposure to carbon dioxide at 40 atm also affected the gas permeability and solubility in the PMSP membranes. These phenomena could be related to a difference in the glassy state of the as-cast membranes synthesized with various catalysts.

引用

页码：261 / 272

页数：12

共 53 条

[11] O2/N2 SELECTIVITY IMPROVEMENT FOR POLYTRIMETHYLSILYLPROPYNE MEMBRANES BY UV-IRRADIATION AND FURTHER ENHANCEMENT BY SUBAMBIENT TEMPERATURE OPERATION [J].

HSU, KK ;

NATARAJ, S ;

THOROGOOD, RM ;

PURI, PS .

JOURNAL OF MEMBRANE SCIENCE, 1993, 79 (01) :1-10

[12] AN INVESTIGATION OF THE HIGH GAS-PERMEABILITY OF POLY (1-TRIMETHYLSILYL-1-PROPYNE) [J].

ICHIRAKU, Y ;

STERN, SA ;

NAKAGAWA, T .

JOURNAL OF MEMBRANE SCIENCE, 1987, 34 (01) :5-18

[13] STUDY ON THE GEOMETRIC STRUCTURE OF POLY[1-(TRIMETHYLSILYL)-1-PROPYNE] BY C-13 AND SI-29 NMR SPECTROSCOPIES [J].

IZUMIKAWA, H ;

MASUDA, T ;

HIGASHIMURA, T .

POLYMER BULLETIN, 1991, 27 (02) :193-199

[14] THE EFFECTS OF CO2 EXPOSURE ON PURE AND MIXED GAS PERMEATION BEHAVIOR - COMPARISON OF GLASSY POLYCARBONATE AND SILICONE-RUBBER [J].

JORDAN, SM ;

KOROS, WJ ;

FLEMING, GK .

JOURNAL OF MEMBRANE SCIENCE, 1987, 30 (02) :191-212

[15] SUBSTITUTED PROPYNE POLYMERS .2. EFFECTS OF AGING ON THE GAS-PERMEABILITY PROPERTIES OF POLY[1-(TRIMETHYLSILYL)PROPYNE] FOR GAS SEPARATION MEMBRANES [J].

LANGSAM, M ;

ROBESON, LM .

POLYMER ENGINEERING AND SCIENCE, 1989, 29 (01) :44-54

[16]

Langsam M., 1988, GAS SEP PURIF, V2, P162, DOI [10.1016/0950-4214(88)80001-X, DOI 10.1016/0950-4214(88)80001-X]

[17] GAS PERMEABILITIES OF POLY(TRIMETHYLSILYLPROPYNE) MEMBRANES SURFACE MODIFIED WITH CF4 PLASMA [J].

LIN, XA ;

JUN, XA ;

YU, YL ;

JIE, C ;

ZHENG, GD ;

XU, JP .

JOURNAL OF APPLIED POLYMER SCIENCE, 1993, 48 (02) :231-236

[18] DIFFUSION AND SOLUTION OF GASES IN SUBSTITUTED POLYACETYLENE MEMBRANES [J].

MASUDA, T ;

IGUCHI, Y ;

TANG, BZ ;

HIGASHIMURA, T .

POLYMER, 1988, 29 (11) :2041-2049

[19] POLY[1-(TRIMETHYLSILYL)-1-PROPYNE] - A NEW HIGH POLYMER SYNTHESIZED WITH TRANSITION-METAL CATALYSTS AND CHARACTERIZED BY EXTREMELY HIGH GAS-PERMEABILITY [J].

MASUDA, T ;

ISOBE, E ;

HIGASHIMURA, T ;

TAKADA, K .

JOURNAL OF THE AMERICAN CHEMICAL SOCIETY, 1983, 105 (25) :7473-7474

[20] THERMAL-DEGRADATION OF POLYACETYLENES CARRYING SUBSTITUENTS [J].

MASUDA, T ;

TANG, BZ ;

HIGASHIMURA, T ;

YAMAOKA, H .

MACROMOLECULES, 1985, 18 (12) :2369-2373

← 1 2 3 4 5 6 →