EFFECTS OF SO2 DEPOSITION ON PAINTED STEEL SURFACES

被引：6

作者：

DAVIS, GD

SHAW, BA

ARAH, CO

FRITZ, TL

MOSHIER, WC

SIMPSON, TC

MORAN, PJ

ZANKEL, KL

机构：

[1] JOHNS HOPKINS UNIV,BALTIMORE,MD 21218

[2] VERSAR INC,COLUMBIA,MD 21045

来源：

SURFACE AND INTERFACE ANALYSIS | 1990年 / 15卷 / 02期

关键词：

D O I：

10.1002/sia.740150208

中图分类号：

O64 [物理化学（理论化学）、化学物理学];

学科分类号：

070304 ; 081704 ;

摘要：

The effects of 1 ppm SO2 with high humidity on alkyd‐painted steel was investigated using x‐ray photoelectron spectroscopy (XPS) and adhesion tensile tests. The SO2 caused a spotted discoloration on the specimens on which dew is allowed to dry and accelerated the loss of adhesion between the primer and the steel. The brown spots are characterized by a high S content and form in areas where the condensed dew becomes more concentrated in H2SO3 or H2SO4 as it evaporates. Specimens not exposed to dew also have high S concentration on the surface, but do not discolor. High humidity alone caused a loss of adhesion at the primer–metal interface, but SO2 increased the rate of this de‐adhesion. Such a loss of adhesion decreases the protection provided by the paint system and the presence of Fe on both sides of some failures indicated that the substrate was beginning to corrode. Copyright © 1990 John Wiley & Sons Ltd.

引用

页码：107 / 112

页数：6

共 24 条

[1]

Ailor WH, 1982, ATMOSPHERIC CORROSIO, Vfirst

[2]

BALIK CM, 1986, REV EVALUATION SCI A

[3] ADVANCES IN CHARGE NEUTRALIZATION FOR XPS MEASUREMENTS OF NONCONDUCTING MATERIALS [J].

BARTH, G ;

LINDER, R ;

BRYSON, C .

SURFACE AND INTERFACE ANALYSIS, 1988, 11 (6-7) :307-311

[4]

CAMPBELL GG, 1974, J PAINT TECHNOL, V46, P59

[5]

CUNNINGHAM GP, 1981, J COATING TECHNOL, V53, P39

[6]

DEAN SW, 1987, MATER PERFORMANCE, V26, P9

[7] EFFECTS OF ACID DEPOSITION ON PAINTS AND METALS - RESULTS OF A CONTROLLED FIELD-STUDY [J].

EDNEY, EO ;

CHEEK, SF ;

STILES, DC ;

CORSE, EW ;

WHEELER, ML ;

SPENCE, JW ;

HAYNIE, FH ;

WILSON, WE .

ATMOSPHERIC ENVIRONMENT, 1988, 22 (10) :2263-2274

[8]

GERLOCK JL, 1985, J COATING TECHNOL, V57, P37

[9]

HAAGENRUD S, 1977, J OIL COLOUR CHEM AS, V60, P469

[10]

HAMMOND JS, 1979, J COATING TECHNOL, V51, P45

← 1 2 3 →