SUPERCONDUCTING PROPERTIES OF YBA2CU3OY TREATED UNDER HIGH-PRESSURE AND HIGH-TEMPERATURE

被引：4

作者：

BOIRE, P

CHATEAU, C

LEGER, JM

SURYANARAYANAN, R

GOROCHOV, O

QUITMANN, C

机构：

[1] CNRS, LAB PHYS SOLIDES BELLEVUE, F-92195 MEUDON, FRANCE

[2] RHEIN WESTFAL TH AACHEN, INST PHYS 2, W-5100 AACHEN, GERMANY

来源：

SUPERCONDUCTOR SCIENCE & TECHNOLOGY | 1991年 / 4卷 / 04期

关键词：

D O I：

10.1088/0953-2048/4/4/002

中图分类号：

O59 [应用物理学];

学科分类号：

摘要：

Pre-reacted YBa2CU3O(y) has been treated under a pressure of 4 GPa in a belt apparatus and at high temperature (950-degrees-C). The sample was characterized by x-ray diffraction, resistivity and magnetization (up to 5 T) measurements. The thermal treatment under high pressure preserves the mean oxygen content and restores fairly good junctions between the grains which have been partly crushed to fill the voids during the compression stage. This contrasts with previous results obtained after non-isostatic pressure treatments which led to semiconducting samples. The intra- and intergrain properties are discussed and compared with those observed on samples prepared under ordinary pressures.

引用

页码：137 / 142

页数：6

共 30 条

[21] ENDURANCE LIMIT OF REVERSIBLE TC INCREASE WITH COMPRESSIVE STRESS OF YBA2CU3O7-Y OXIDE [J].