DAMAGE PROFILES IN MGO SINGLE-CRYSTALS AFTER KRYPTON IMPLANTATION

被引：6

作者：

FRIEDLAND, E

机构：

[1] Department of Physics, University of Pretoria, Pretoria

来源：

NUCLEAR INSTRUMENTS & METHODS IN PHYSICS RESEARCH SECTION B-BEAM INTERACTIONS WITH MATERIALS AND ATOMS | 1993年 / 80-1卷

关键词：

D O I：

10.1016/0168-583X(93)96091-P

中图分类号：

TH7 [仪器、仪表];

学科分类号：

0804 ; 080401 ; 081102 ;

摘要：

Single crystals of magnesium oxide were implanted with 150 keV krypton ions at room temperature. Fluences ranged from 5 x 10(14) to 5 x 10(15) at. cm-2 with dose rates well below 10(13) at. cm-2 s-1 to prevent target heating. Defect profiles were obtained by fitting aligned alpha-particle backscattering spectra to a dechanneling rate equation. For the lowest fluence the depth profile of the damaged region agrees reasonably with theoretical estimates, whilst at higher fluences a significantly increased depth of the damaged region is found. The energy dependence of dechanneling as well as the general shape of the aligned backscattering spectra indicate a defect structure consisting of a combination of dislocation loops and severely disordered regions.

引用

页码：128 / 131

页数：4

共 17 条

[11] IRON-ION IMPLANTATION EFFECTS IN MGO CRYSTALS [J].

PEREZ, A ;

MAREST, G ;

SAWICKA, BD ;

SAWICKI, JA ;

TYLISZCZAK, T .

PHYSICAL REVIEW B, 1983, 28 (03) :1227-1238

[12] ION-IMPLANTATION EFFECTS IN CRYSTALLINE INORGANIC INSULATORS [J].

PEREZ, A .

NUCLEAR INSTRUMENTS & METHODS IN PHYSICS RESEARCH SECTION B-BEAM INTERACTIONS WITH MATERIALS AND ATOMS, 1984, 1 (2-3) :621-627

[13] SPINEL FERRITE FORMATION IN IRON IMPLANTED MGO CRYSTALS [J].

PEREZ, A ;

TREILLEUX, M ;

FRITSCH, L ;

MAREST, G .

NUCLEAR INSTRUMENTS & METHODS, 1981, 182 (APR) :747-751

[14] DECHANNELLING CYLINDER OF DISLOCATIONS [J].

QUERE, Y .

PHYSICA STATUS SOLIDI, 1968, 30 (02) :713-&

[15]

RIMINI E, 1976, ION BEAM SURFACE LAY, P597

[16]

Ziegler J.F., 1985, STOPPING RANGES IONS

[17]

ZIEGLER JF, 1985, HELIUM STOPPING POWE

← 1 2 →