CONTINUOUS MICROSCRATCH MEASUREMENTS OF THIN-FILM ADHESION STRENGTHS

被引:18
作者
VENKATARAMAN, SK
NELSON, JC
HSIEH, AJ
KOHLSTEDT, DL
GERBERICH, WW
机构
[1] UNIV MINNESOTA,DEPT CHEM ENGN & MAT SCI,MINNEAPOLIS,MN 55455
[2] USA,MAT TECHNOL LAB,WATERTOWN,MA 02172
[3] UNIV MINNESOTA,DEPT GEOL & GEOPHYS,MINNEAPOLIS,MN 55455
关键词
ADHESION; THIN FIRMS; MICROSCRATCH; TOUGHNESS;
D O I
10.1163/156856193X00105
中图分类号
TQ [化学工业];
学科分类号
0817 ;
摘要
The adhesion strengths of metal/ceramic, metal/polymer, and polymer/polymer interfaces have been characterized using the continuous microscratch technique. In these experiments, a conical diamond indenter was driven simultaneously into a thin film at a rate of 15 nm/s and across the film surface at a rate of 0.5 mu m/s until a load drop or other discontinuity occurred, indicating film failure. The critical load at failure of the thin film was taken as a measure of the adhesion strength. For metal/ceramic systems such as Cr thin films on Al2O3, and for diamond-like-carbon (DLC) films on glass, clear load drops provided an accurate measure of the adhesion strengths. For metal/polymer systems such as Cu thin films on PET, a change in the loading pattern and periodic cracking events along the scratch track provided evidence of film delamination. For DLC films on polycarbonate substrates, the carbon thin film cracked before it delaminated. For bulk polymers such as polycarbonate and polystyrene/polypropylene, crack growth occurred by a stick-slip mechanism. Using a model developed in an earlier paper, the practical work of adhesion for the Cr/Al2O3 system was determined to be 0.09 J/m(2) and that for the DLC/polycarbonate system was 0.05 J/m(2). The fracture toughnesses of the polycarbonate and polystyrene were 0.81 and 0.2 MPa m(1/2), respectively. These numbers are in good agreement with those obtained by other methods for these systems.
引用
收藏
页码:1279 / 1292
页数:14
相关论文
共 25 条
[1]   ULTIMATE SHEAR STRENGTHS OF COPPER SILICA AND NICKEL SILICA INTERFACES [J].
AGRAWAL, DC ;
RAJ, R .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1990, 126 :125-131
[2]   MEASUREMENT OF ADHESION OF THIN FILMS [J].
BENJAMIN, P ;
WEAVER, C .
PROCEEDINGS OF THE ROYAL SOCIETY OF LONDON SERIES A-MATHEMATICAL AND PHYSICAL SCIENCES, 1960, 254 (1277) :163-176
[3]   THE USE OF SCRATCH ADHESION TESTING FOR THE DETERMINATION OF INTERFACIAL ADHESION - THE IMPORTANCE OF FRICTIONAL DRAG [J].
BULL, SJ ;
RICKERBY, DS ;
MATTHEWS, A ;
LEYLAND, A ;
PACE, AR ;
VALLI, J .
SURFACE & COATINGS TECHNOLOGY, 1988, 36 (1-2) :503-517
[4]   THE MECHANICAL-PROPERTIES OF WEAR-RESISTANT COATINGS .2. EXPERIMENTAL STUDIES AND INTERPRETATION OF HARDNESS [J].
BURNETT, PJ ;
RICKERBY, DS .
THIN SOLID FILMS, 1987, 148 (01) :51-65
[5]   THE MECHANICAL-PROPERTIES OF WEAR-RESISTANT COATINGS .1. MODELING OF HARDNESS BEHAVIOR [J].
BURNETT, PJ ;
RICKERBY, DS .
THIN SOLID FILMS, 1987, 148 (01) :41-50
[6]  
EVANS AG, 1990, MRS B, V46
[7]  
FABES BD, 1990, MATER RES SOC SYMP P, V188, P127, DOI 10.1557/PROC-188-127
[8]   MEASUREMENT OF INTERFACE STRENGTH BY A LASER SPALLATION TECHNIQUE [J].
GUPTA, V ;
ARGON, AS ;
PARKS, DM ;
CORNIE, JA .
JOURNAL OF THE MECHANICS AND PHYSICS OF SOLIDS, 1992, 40 (01) :141-180
[9]   THE MECHANICAL-PROPERTIES OF THIN-FILMS - A REVIEW [J].
HARDWICK, DA .
THIN SOLID FILMS, 1987, 154 (1-2) :109-124
[10]  
HOFFMAN RW, 1989, MATER RES SOC S P, V130, P295