EPITAXIAL Tl2Ba2Ca2Cu3O10 FILMS WITH VERY LOW MICROWAVE SURFACE RESISTANCE UP TO 110 K

被引：27

作者：

Holstein, W. L. ^{[1
]}

Parisi, L. A. ^{[1
]}

Wilker, C. ^{[1
]}

Flippen, R. B. ^{[1
]}

机构：

[1] Dupont Co, Cent Res & Dev, POB 80304, Wilmington, DE 19880 USA

来源：

IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY | 1993年 / 3卷 / 01期

关键词：

D O I：

10.1109/77.233337

中图分类号：

TM [电工技术]; TN [电子技术、通信技术];

学科分类号：

0808 ; 0809 ;

摘要：

Very low surface resistance epitaxial Tl2Ba2Ca2Cu3O10 films have been prepared on one or both sides of (100) LaAlO3 substrates up to 5 cm (2 inches) in diameter. The T-c of the films was 120.5 +/- 0.5 K as measured by ac magnetic susceptibility. Surface resistance at 10 GHz measured with an HTS-sapphire resonator was 24 +/- 10 mu Omega at 4.2 K, 181 +/- 10 mu Omega at 77 K, and 359 +/- 20 mu Omega at 100 K. Identical T-c and surface resistance were observed for films prepared on both sides of substrates. A microstrip resonator prepared from a double side-coated film on a LaAlO3 substrate exhibited an unloaded Q-value of 7200 at 100 K and 8.7 GHz and continued to demonstrate performance superior to similar copper resonators even at 115 K. This is the highest temperature reported to date for operation of a superconducting device.

引用

页码：1197 / 1200

页数：4

共 15 条

[11] BULK SUPERCONDUCTIVITY AT 120-K IN THE TL-CA BA-CU-O SYSTEM [J].

SHENG, ZZ ;

HERMANN, AM .

NATURE, 1988, 332 (6160) :138-139

[12] BULK SUPERCONDUCTIVITY UP TO 122-K IN THE TL-PB-SR-CA-CU-O SYSTEM [J].

SUBRAMANIAN, MA ;

TORARDI, CC ;

GOPALAKRISHNAN, J ;

GAI, PL ;

CALABRESE, JC ;

ASKEW, TR ;

FLIPPEN, RB ;

SLEIGHT, AW .

SCIENCE, 1988, 242 (4876) :249-252

[13] CRYSTAL-STRUCTURE OF THE HIGH-TEMPERATURE SUPERCONDUCTOR TL2BA2CACU2O8 [J].

SUBRAMANIAN, MA ;

CALABRESE, JC ;

TORARDI, CC ;

GOPALAKRISHNAN, J ;

ASKEW, TR ;

FLIPPEN, RB ;

MORRISSEY, KJ ;

CHOWDHRY, U ;

SLEIGHT, AW .

NATURE, 1988, 332 (6163) :420-422

[14] 5-GHZ HIGH-TEMPERATURE-SUPERCONDUCTOR RESONATORS WITH HIGH-Q AND LOW-POWER DEPENDENCE UP TO 90K [J].

WILKER, C ;

SHEN, ZY ;

PANG, P ;

FACE, DW ;

HOLSTEIN, WL ;

MATTHEWS, AL ;

LAUBACHER, DB .

IEEE TRANSACTIONS ON MICROWAVE THEORY AND TECHNIQUES, 1991, 39 (09) :1462-1467

[15]

Wilker C., 1992, 1992 APPL SUP C AUG

← 1 2 →