EXISTENCE OF PREFERENTIAL SURFACE DEFORMATION IN COPPER SINGLE CRYSTALS

被引：6

作者：

BLOCK, RJ

JOHNSON, RM

机构：

[1] Department of Chemical Engineering and Materials Science, University of Oklahoma, Norman, OklahomaJapan

[2] Department of Engineering Mechanics, University of Texas at Arlington

来源：

ACTA METALLURGICA | 1969年 / 17卷 / 03期

关键词：

D O I：

10.1016/0001-6160(69)90070-4

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

The dislocation density of deformed copper single crystals was determined at various depths from the original crystal surface. No variation was found to depths greater than 500 μ. On the basis of these experiments and a consideration of the literature, the existence of a near surface debris layer in copper was considered unlikely. © 1969.

引用

页码：299 / &

共 28 条

[11]

KRAMER IR, 1963, T METALL SOC AIME, V227, P1003

[12]

KRAMER IR, 1965, T METALL SOC AIME, V233, P1462

[13]

KRAMER IR, 1964, T METALL SOC AIME, V230, P991

[14]

KRAMER IR, 1961, T METALL SOC AIME, V221, P780

[15] COMMENTS ON DISLOCATION DISTRIBUTION NEAR SURFACE OF DEFORMED COPPER [J].

KRAMER, IR ;

HAEHNER, CL .

ACTA METALLURGICA, 1967, 15 (04) :678-&

[16]

KRAMER IR, 1961, T METALL SOC AIME, V221, P989

[17]

KRAMER IR, 1966, ENVIRONMENT SENSITIV, P127

[18]

KRAMER IR, 1966, ENVIRONMENT SENSITIV, P208

[19] DENSITY AND DISTRIBUTION OF DISLOCATIONS IN DEFORMED COPPER CRYSTALS [J].

LIVINGSTON, JD .

ACTA METALLURGICA, 1962, 10 (MAR) :229-&

[20] ETCH PITS AT DISLOCATIONS IN COPPER [J].

LIVINGSTON, JD .

JOURNAL OF APPLIED PHYSICS, 1960, 31 (06) :1071-1076

← 1 2 3 →