FATIGUE OF VISCOELASTIC POLYMERS .2. FRACTOGRAPHY

The results of a fractographic study of fatigue failure in viscoelastic polymers is presented. Tests were conducted on a spherulitic low-density polyethylene in reversed loading using non-symmetrical deformation conditions. The microfractographic features have been found to depend on the deformation programme, the temperature of the test and the position on the fracture surface. The latter has been related to the different stages of growth revealed by plotting crack-growth propagation data. As well as interspherulitic fracture, other mechanisms that are sometimes prevalent involve cold-drawing, (fibrillation), and/or lamellar reorientation. The appearance of fatigue fracture surfaces of a non-spherulitic low-density polyethylene, a high-density polyethylene and a plasticized poly(vinyl chloride) corroborate the structural interpretations proposed to account for the observations with the spherulitic low-density polyethylene. © 1979.