MARTENSITE FORMATION IN TI-AL LAYERS PRODUCED BY LASER SURFACE ALLOYING

被引:14
作者
ABBOUD, JH
WEST, DRF
机构
[1] Department of Materials, Imperial College of Science, Technology and Medicine, London
关键词
D O I
10.1179/mst.1991.7.9.827
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The microstructures of Ti-Al layers produced by laser surface alloying of a Ti substrate have been investigated for Al contents in the range 17-36 at.-%. The alloyed layers were obtained using a continuous wave CO2 laser and a powder feed technique employing the following laser processing parameters: 1.8 kW power, 3 mm beam diameter, 7 mm s-1 traverse speed, and feedrates of Al powder ranging from 0.03 to 0.07 g s-1. The microstructures were disordered lath martensite alpha' in 17 at.-% Al alloy, ordered massive and acicular martensite in 23 at.-% Al alloy, and ordered massive, acicular, and lath martensite in 30 and 36 at.-% Al alloys. The change in martensite type and morphology is discussed in relation to the available data for the beta to alpha' transformation in Ti alloys.
引用
收藏
页码:827 / 834
页数:8
相关论文
共 22 条
[21]   RAPID SOLIDIFICATION PROCESSING OF TITANIUM-ALLOYS [J].
SASTRY, SML ;
PENG, TC ;
MESCHTER, PJ ;
ONEAL, JE .
JOURNAL OF METALS, 1983, 35 (09) :21-28
[22]  
Sato T., 1960, J AUST I MET, V5, P149