MECHANICAL DEGRADATION OF MGO BY WATER VAPOR

被引：10

作者：

JANOWSKI, KR

ROSSI, RC

机构：

[1] Aerospace Corporation, EI Segundo, California

来源：

JOURNAL OF THE AMERICAN CERAMIC SOCIETY | 1968年 / 51卷 / 08期

关键词：

D O I：

10.1111/j.1151-2916.1968.tb11918.x

中图分类号：

TQ174 [陶瓷工业]; TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

The effect of exposure to the laboratory atmosphere on the fracture stress and Young's modulus of poly crystalline magnesium oxide was studied. The observed degradation of mechanical properties was attributed to chemical attack by atmospheric water vapor. The rate and extent of degradation depended on the amount and nature of porosity in the specimens. Copyright © 1968, Wiley Blackwell. All rights reserved

引用

页码：453 / &

共 20 条

[11] SURFACE HYDROXYL IN MGO [J].

NIELSEN, TH ;

LEIPOLD, MH .

JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1966, 49 (11) :626-&

[12] DELAYED FRACTURE OF SINTERED ALUMINA [J].

PEARSON, S .

PROCEEDINGS OF THE PHYSICAL SOCIETY OF LONDON SECTION B, 1956, 69 (12) :1293-1296

[13]

Pearson S., 1949, P PHYS SOC B, V62, P469

[14]

RICE RW, 1967, AM CERAM SOC BULL, V46, P363

[15]

RICE RW, 1967, 69 AM CER SOC ANN M

[16]

ROBERTS JP, 1952, SELECTED GOVT RESEAR, V10, P51

[17] ON THE STRENGTH OF GLASS IN WATER VAPOR [J].

SCHOENING, FRL .

JOURNAL OF APPLIED PHYSICS, 1960, 31 (10) :1779-1784

[18]

SPINNER S, 1961, AM SOC TEST MATER PR, V61, P1221

[19]

SPRIGGS RM, 1963, J AM CERAM SOC, V46, P225

[20]

Williams L.S., 1956, BRIT CERAM T, V55, P287

← 1 2 →