PREPARATION AND PROPERTIES OF ISOTACTIC AND SYNDIOTACTIC POLY(METHYL METHACRYLATE)S, UNIFORM WITH RESPECT TO MOLECULAR-WEIGHT

Highly isotactic (it-) and highly syndiotactic (st-) poly(methyl methacrylate)s (PMMAs) uniform with respect to molecular weight (stereoregular, uniform PMMAs) were isolated up to the 100mer from it- and st-PMMAs by supercritical fluid chromatography (SFC) and characterized by NMR and mass spectroscopies. Glass transition temperatures (Tg's) of the uniform it- and st-PMMAs were higher than those of the corresponding PMMAs with MWD and with similar molecular weight on average. The Tg values of the uniform it- and st-PMMAs series obeyed the relationship, Tg = Tginfinity - K/M, where M and Tginfinity denote molecular weight and Tg at infinite M, respectively. The reciprocal melting points (1/Tm) of uniform it-PMMA (degree of polymerization, DP = 28-44), obtained from methanol solutions by evaporating the solvent, increased linearly with increasing 1/DP. Extrapolation of the linear relation to 1/DP = 0 gave the Tm of it-PMMA with infinite DP; Tminfinity = 171.1-degree-C. Thermal degradation behavior was studied by thermogravimetry and by SFC analysis of degradation products. In gel-permeation chromatography (GPC) measurements, the it-50mer eluted faster than the st-50mer. Calibration curves for it- and st-PMMAs could be obtained using series of the uniform PMMAs. The instrumental spreading factor determined using it-25mer, it-50mer, st-25mer and st-50mer for our GPC chromatograph was 0.07 ml when the volume of the sample solution was 0.003ml. GPC analysis of a mixture of the it- and st-50mers in tetrahydrofuran indicated formation of a stereocomplex in the solution, and was found quite useful to elucidate the minimum sequence length required for complex formation.