DEFORMATION RESISTANCE IN ORIENTED NYLON-6

被引:109
作者
LIN, L [1 ]
ARGON, AS [1 ]
机构
[1] MIT,DEPT MECH ENGN,CAMBRIDGE,MA 02139
关键词
D O I
10.1021/ma00041a025
中图分类号
O63 [高分子化学(高聚物)];
学科分类号
070305 ; 080501 ; 081704 ;
摘要
Initially spherulitic nylon 6 was textured into a quasi-single crystal form by plane-strain compression at 170-degrees-C in a deep channel-die to a compression ratio of 4.0, followed by cooling under pressure to room temperature. The resulting material, having orthotropic symmetry with quasi-single crystalline perfection, had a dual morphology in which the normals of the crystallographic (100) planes equipartition at +/-21-degrees with respect to the constraint direction of the plane-strain deformation. This highly textured material, having relatively large dimensions in all directions, was used to study the elastic and plastic anisotropy of the actual constituent lamellar crystallites. As a result, a complete set of nine elastic compliances of the orthotropic sample were measured by a simple direct technique and were related to the monoclinic crystal properties. In addition, detailed measurements were made of the plastic anisotropy of this textured material to establish that plastic response of the actual monoclinic nylon 6 crystallites is derived principally from three crystallographic slip processes consisting of the (001) [010] and (100) [010] chain slip systems and the (001)-[100] transverse slip system. The plastic shear resistances of all these slip systems were found to increase substantially with increasing compressive stress acting across the slip planes. Among these three deformation mechanisms, (001)[010] chain slip is the easiest system to be activated.
引用
收藏
页码:4011 / 4024
页数:14
相关论文
共 75 条
[21]   STRAIN-RATE, TEMPERATURE AND PRESSURE DEPENDENCE OF YIELD OF ISOTROPIC POLY(METHYLMETHACRYLATE) AND POLY(ETHYLENE TEREPHTHALATE) [J].
DUCKETT, RA ;
RABINOWITZ, S ;
WARD, IM .
JOURNAL OF MATERIALS SCIENCE, 1970, 5 (10) :909-+
[22]   DEFORMATION PROCESSES IN POLYETHYLENE INTERPRETED IN TERMS OF CRYSTAL PLASTICITY [J].
FRANK, FC ;
KELLER, A ;
OCONNOR, A .
PHILOSOPHICAL MAGAZINE, 1958, 3 (25) :64-&
[23]   DECONVOLUTION OF X-RAY-DIFFRACTION DATA TO ELUCIDATE PLASTIC-DEFORMATION MECHANISMS IN THE UNIAXIAL EXTENSION OF BULK NYLON-6 [J].
GALESKI, A ;
ARGON, AS ;
COHEN, RE .
MACROMOLECULES, 1991, 24 (13) :3945-3952
[24]   MORPHOLOGY OF BULK NYLON-6 SUBJECTED TO PLANE-STRAIN COMPRESSION [J].
GALESKI, A ;
ARGON, AS ;
COHEN, RE .
MACROMOLECULES, 1991, 24 (13) :3953-3961
[25]   CHANGES IN THE MORPHOLOGY OF BULK SPHERULITIC NYLON-6 DUE TO PLASTIC-DEFORMATION [J].
GALESKI, A ;
ARGON, AS ;
COHEN, RE .
MACROMOLECULES, 1988, 21 (09) :2761-2770
[26]  
GALESKI A, 1987, MAKROMOL CHEM, V188, P1195
[27]   POLYMER DEFORMATION .4. DRAWING OF NYLON 6 + POLYOXYMETHYLENE CRYSTALS [J].
GEIL, PH .
JOURNAL OF POLYMER SCIENCE PART A-GENERAL PAPERS, 1964, 2 (9PA) :3857-&
[28]  
GEIL PH, 1964, J POLYM SCI A, V2, P3818
[29]   YIELD AND TRANSIENT EFFECTS DURING THE PLASTIC-DEFORMATION OF SOLID POLYMERS [J].
GSELL, C ;
JONAS, JJ .
JOURNAL OF MATERIALS SCIENCE, 1981, 16 (07) :1956-1974
[30]   ANISOTROPY IN ORIENTED FIBRES FROM SYNTHETIC POLYMERS [J].
HADLEY, DW ;
PINNOCK, PR ;
WARD, IM .
JOURNAL OF MATERIALS SCIENCE, 1969, 4 (02) :152-&