MACROPARTICLE-FREE TIN FILMS PREPARED BY ARC ION-PLATING PROCESS

被引:20
作者
KANG, GH [1 ]
UCHIDA, H [1 ]
KOH, ES [1 ]
机构
[1] TOKAI UNIV,DEPT MAT SCI & ENGN,HIRATSUKA,KANAGAWA 25912,JAPAN
关键词
D O I
10.1016/0257-8972(94)90151-1
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
TiN thin films prepared by the are ion-plating process usually have a significant quantity of macroparticles on their surface. In this experiment a rotating target was used to apply the centrifugal effect to prevent the formation of macroparticles on the surface of TiN thin films. The number of macroparticles was measured using an image analysis method and investigated as a function of the rotational velocity of the target. When the rotational velocity was over 3000 rev min(-1), the number of macroparticles on the film surface was markedly reduced. When the rotational velocity was higher than 4200 rev min(-1), the him surface became almost macroparticle free.
引用
收藏
页码:141 / 145
页数:5
相关论文
共 19 条
[1]   REDUCTION IN MACROPARTICLES DURING THE DEPOSITION OF TIN FILMS PREPARED BY ARC ION PLATING [J].
AKARI, K ;
TAMAGAKI, H ;
KUMAKIRI, T ;
TSUJI, K .
SURFACE & COATINGS TECHNOLOGY, 1990, 43-4 (1-3) :312-323
[2]  
Aksenov I. I., 1984, Soviet Physics - Technical Physics, V29, P893
[3]   ION FLUX CHARACTERISTICS IN ARC VAPOR-DEPOSITION OF TIN [J].
BERGMAN, C .
SURFACE & COATINGS TECHNOLOGY, 1988, 36 (1-2) :243-255
[4]   HARD COATINGS OF TIN, (TIHF)N AND (TINB)N DEPOSITED BY RANDOM AND STEERED ARC EVAPORATION [J].
BOELENS, S ;
VELTROP, H .
SURFACE & COATINGS TECHNOLOGY, 1987, 33 (1-4) :63-71
[5]   THE INTERACTION BETWEEN PLASMA AND MACROPARTICLES IN A MULTI-CATHODE-SPOT VACUUM-ARC [J].
BOXMAN, RL ;
GOLDSMITH, S .
JOURNAL OF APPLIED PHYSICS, 1981, 52 (01) :151-161
[6]   FAST DEPOSITION OF METALLURGICAL COATINGS AND PRODUCTION OF SURFACE ALLOYS USING A PULSED HIGH-CURRENT VACUUM-ARC [J].
BOXMAN, RL ;
GOLDSMITH, S ;
SHALEV, S ;
YALOZ, H ;
BROSH, N .
THIN SOLID FILMS, 1986, 139 (01) :41-52
[7]   CATHODE SPOTS AND VACUUM ARCS [J].
DAALDER, JE .
PHYSICA B & C, 1981, 104 (1-2) :91-106
[8]   COMPONENTS OF CATHODE EROSION IN VACUUM ARCS [J].
DAALDER, JE .
JOURNAL OF PHYSICS D-APPLIED PHYSICS, 1976, 9 (16) :2379-+
[9]   EROSION STRUCTURES ON CATHODES ARCED IN VACUUM [J].
DAALDER, JE .
JOURNAL OF PHYSICS D-APPLIED PHYSICS, 1979, 12 (10) :1769-&
[10]   COMPARISON OF THE STEERED ARC AND RANDOM ARC TECHNIQUES [J].
ERTURK, E ;
HEUVEL, HJ ;
DEDERICHS, HG .
SURFACE & COATINGS TECHNOLOGY, 1989, 39 (1-3) :455-464